GaInAsP/InP Integrated Twin-Guide Lasers with First-Order Distributed Bragg Reflectors at 1.3 µm Wavelength

GaInAsP/InP integrated twin-guide lasers with first-order distributed Bragg reflectors (DBR-ITG lasers) were fabricated and operated at room-temperature with a single longitudinal mode. By changing the corrugation period, the central wavelength could be varied in the wavelength range of 1.2~1.3 µm with a single longitudinal mode at temperatures between 150 and 300 K. At room-temperature, the threshold current density and the differential quantum efficiency were 10.4 kA/cm2 and 11.7%, respectively. The refractive index of the quaternary composition was measured and found to be in relatively good agreement with the estimated value. "GaInAsP/InP Integrated Twin-Guide Lasers with First-Order Distributed Bragg Reflectors at 1.3 µm Wavelength"

[1] S. Arai,et al. Conditions of LPE Growth for Lattice Matched GaInAsP/InP DH Lasers with (100) Substrate in the Range of 1.2–1.5 µm , 1978 .

[2] Shigehisa Arai,et al. Low Threshold Current Density (100) GaInAsP/InP Double-Heterostructure Lasers for Wavelength 1.3 µm , 1979 .