Stainless-steel-AlN cermet selective surfaces deposited by direct current magnetron sputtering technology

Abstract Stainless-steel–AlN cermet selective surfaces were deposited by a direct-current (DC) magnetron sputtering technology. The aluminum nitride ceramic and stainless-steel (SS) components in the cermet were deposited by simultaneously running both SS and Al metal targets in a gas mixture of argon and nitrogen. Nitrogen partial pressure was set sufficiently high to ensure that a nearly pure AlN ceramic sublayer was deposited by DC reactive sputtering. Because of the excellent nitriding resistance of stainless steel and the very low nitrogen partial pressure, a nearly pure SS sublayer was deposited by DC sputtering. By substrate rotation, a multi-sublayer system, consisting of alternating SS and AlN sublayers, was deposited. By controlling the thickness of SS and AlN sublayers this multi-sublayer system can be considered as a macrohomogeneous cermet layer. Following this procedure, the SS–AlN cermet selective surfaces with a double cermet layer structure were deposited. The deposited films have the following structure: a low metal volume fraction cermet layer is placed on a high metal volume fraction cermet layer which in turn is placed on an aluminum metal infrared reflection layer. The top surface layer consists of an aluminum nitride anti-reflection layer. A solar absorptance of 0.93–0.96 and normal emittance of 0.03–0.04 at room temperature have been achieved for the SS–AlN cermet selective surfaces. After vacuum baking at 500°C for 1 h there is only a slight change in optical reflectance in the wavelength range of 0.3–2.0 μm for the SS–AlN cermet selective surfaces. However, the values of solar absorptance and emittance change insignificantly, around 0.005.

[1]  H. Pulker,et al.  Properties of reactively d.c.-magnetron-sputtered A1N thin films , 1993 .

[2]  D. Mills,et al.  High solar performance selective surface using bi-sublayer cermet film structures , 1992 .

[3]  David R. Mills,et al.  New cermet film structures with much improved selectivity for solar thermal applications , 1992 .

[4]  G. Harding.  Sputtered metal carbide solar‐selective absorbing surfaces , 1976 .

[5]  G. Niklasson,et al.  Surfaces for selective absorption of solar energy: an annotated bibliography 1955–1981 , 1983 .

[6]  G. L. Harding,et al.  Cylindrical magnetron sputtering system for coating solar selective surfaces onto batches of tubes , 1979 .

[7]  D. Mills,et al.  High efficiency MoAl2O3 cermet selective surfaces for high-temperature application , 1996 .

[8]  G. Harding,et al.  Optical properties of d.c. reactively sputtered thin films , 1984 .

[9]  Jai-Young Lee,et al.  Influence of sputtering pressure on the microstructure evolution of AlN thin films prepared by reactive sputtering , 1995 .

[10]  G. L. Harding,et al.  Progress in the materials science of all-glass evacuated collectors , 1984 .

[11]  C. Granqvist,et al.  Materials science for solar energy conversion systems , 1991 .

[12]  David R. Mills,et al.  Very low‐emittance solar selective surfaces using new film structures , 1992 .

[13]  Santa Cruz,et al.  Solar collectors, energy storage, and materials , 1990 .

[14]  G. Harding,et al.  Composition, optical properties and degradation modes of Cu/(graded metal-carbon) solar selective surfaces , 1983 .

[15]  M. Penza,et al.  Low temperature growth of r.f. reactively planar magnetron-sputtered AlN films , 1995 .

[16]  S. Berthier,et al.  Optical properties of substoichiometric TiNx , 1981 .

[17]  C. Granqvist,et al.  SELECTIVELY SOLAR-ABSORBING SURFACE COATINGS: OPTICAL PROPERTIES AND DEGRADATION , 1991 .