Deformation and damage upon stretching of degradable polymers (PLA and PCL)

Microstructure and plastic behavior of poly(lactic acid), PLA, and poly(e-caprolactone), PCL, are investigated. The injected molded specimens are analyzed as received. Thermomechanical properties are characterized by DSC and DMA and crystalline structure by WAXS. The results show that PLA samples are weakly crystalline (14 wt%) and that amorphous phase is glassy at room temperature. The PCL samples exhibit higher crystallinity (53 wt%) and contain a rubber-like amorphous phase. Mechanical behavior is investigated by means of novel video-controlled materials testing system specially developed to assess true stress vs. true strain curves and to record the volume changes upon stretching. While tested at 50 °C, PLA undergoes extensive plastic deformation with a dramatic yield softening followed by a progressively increasing strain hardening. Volume strain, which characterizes deformation damage, increases steadily over the whole plastic stage until reaching 0.27 for an axial strain of 1, 4. For its part, PCL exhibits at 23 °C a much progressive plastic response with a soft yield point, no softening, and moderate strain hardening at large strain. Volume change is delayed until axial strain reaches 0.4. Subsequent damage grows very quickly, eventually reaching 0.2 for an ultimate strain of 1, 3. Results are discussed on the basis of microscopic damage mechanisms observed in the stretched state.

[1]  J. Jonas,et al.  Yield and transient effects during the plastic deformation of solid polymers , 1981 .

[2]  J. Chalmers,et al.  Characterization of the Degradation of Polylactic Acid Polymer in a Solid Substrate Environment , 1998, Biotechnology progress.

[3]  M. Arroyo,et al.  Thermal and dynamic mechanical properties of polypropylene and short organic fiber composites , 2000 .

[4]  L. Avérous,et al.  Properties of thermoplastic blends: starch-polycaprolactone , 2000 .

[5]  C. G'sell,et al.  Experimental characterization of deformation damage in solid polymers under tension, and its interrelation with necking , 2002 .

[6]  Stephen P. McCarthy,et al.  Reactive compatibilization of biodegradable blends of poly(lactic acid) and poly(ε-caprolactone) , 1998 .

[7]  S. Lim,et al.  Toughening of polylactide by melt blending with linear low‐density polyethylene , 2003 .

[8]  R. Ruseckaite,et al.  Structural changes of polylactic‐acid (PLA) microspheres under hydrolytic degradation , 1999 .

[9]  S. Huang,et al.  The hydrolysis of poly(lactic acid)/ poly(hexamethylene succinate) blends , 1998 .

[10]  N. Washburn,et al.  Structure and mechanical properties of poly(?,?-lactic acid)/poly(ɛ-caprolactone) blends , 2003 .

[11]  A. Albertsson,et al.  The biodegradation of amorphous and crystalline regions in film-blown poly(ε-caprolactone) , 2000 .

[12]  A. Pennings,et al.  Crystal structure, conformation and morphology of solution-spun poly(L-lactide) fibers , 1990 .

[13]  K. Nitta,et al.  Tensile yield of isotactic polypropylene in terms of a lamellar-cluster model , 2000 .

[14]  J. Jonas,et al.  Determination of the plastic behaviour of solid polymers at constant true strain rate , 1979 .

[15]  Michel Vert,et al.  Effects of morphology, conformation and configuration on the IR and Raman spectra of various poly(lactic acid)s , 1998 .

[16]  E. Martuscelli,et al.  Preparation and characterisation of compatibilised polycaprolactone/starch composites , 2000 .

[17]  Lijia An,et al.  Crystallization behavior of PCL in hybrid confined environment , 2001 .

[18]  L. Avérous,et al.  Poly(lactic acid): plasticization and properties of biodegradable multiphase systems , 2001 .

[19]  J. Lunt Large-scale production, properties and commercial applications of polylactic acid polymers , 1998 .

[20]  S. Tjong,et al.  Compatibility and degradation of blends of poly(caprolactone)–poly(ethylene glycol) block copolymer and polypropylene , 1999 .

[21]  Lijian Liu,et al.  Selective Enzymatic Degradations of Poly(l-lactide) and Poly(ε-caprolactone) Blend Films , 2000 .