Conducting-polymer nanotubes improve electrical properties, mechanical adhesion, neural attachment, and neurite outgrowth of neural electrodes.

An in vitro comparison of conducting-polymer nanotubes of poly(3,4-ethylenedioxythiophene) (PEDOT) and poly(pyrrole) (PPy) and to their film counterparts is reported. Impedance, charge-capacity density (CCD), tendency towards delamination, and neurite outgrowth are compared. For the same deposition charge density, PPy films and nanotubes grow relatively faster vertically, while PEDOT films and nanotubes grow more laterally. For the same deposition charge density (1.44 C cm(-2)), PPy nanotubes and PEDOT nanotubes have lower impedance (19.5 +/- 2.1 kOmega for PPy nanotubes and 2.5 +/- 1.4 kOmega for PEDOT nanotubes at 1 kHz) and higher CCD (184 +/- 5.3 mC cm(-2) for PPy nanotubes and 392 +/- 6.2 mC cm(-2) for PEDOT nanotubes) compared to their film counterparts. However, PEDOT nanotubes decrease the impedance of neural-electrode sites by about two orders of magnitude (bare iridium 468.8 +/- 13.3 kOmega at 1 kHz) and increase capacity of charge density by about three orders of magnitude (bare iridium 0.1 +/- 0.5 mC cm(-2)). During cyclic voltammetry measurements, both PPy and PEDOT nanotubes remain adherent on the surface of the silicon dioxide while PPy and PEDOT films delaminate. In experiments of primary neurons with conducting-polymer nanotubes, cultured dorsal root ganglion explants remain more intact and exhibit longer neurites (1400 +/- 95 microm for PPy nanotubes and 2100 +/- 150 microm for PEDOT nanotubes) than their film counterparts. These findings suggest that conducting-polymer nanotubes may improve the long-term function of neural microelectrodes.

[1]  Mohammad Reza Abidian,et al.  Multifunctional Nanobiomaterials for Neural Interfaces , 2009 .

[2]  Xinyan Tracy Cui,et al.  Electrochemically controlled release of dexamethasone from conducting polymer polypyrrole coated electrode. , 2006, Journal of controlled release : official journal of the Controlled Release Society.

[3]  E. Smela,et al.  Microfabricating conjugated polymer actuators. , 2000, Science.

[4]  Geoffrey M. Spinks,et al.  Conducting polymers - bridging the bionic interface. , 2007, Soft matter.

[5]  D. Szarowski,et al.  Brain responses to micro-machined silicon devices , 2003, Brain Research.

[6]  K Isahara,et al.  The interaction of vascular endothelial cells and dorsal root ganglion neurites is mediated by vitronectin and heparan sulfate proteoglycans. , 1995, Brain research. Developmental brain research.

[7]  R. Misra,et al.  Biomaterials , 2008 .

[8]  Thomas M. McKenna,et al.  Enabling Technologies for Cultured Neural Networks , 1994 .

[9]  Elisabeth Smela,et al.  Color and Volume Change in PPy(DBS) , 2009 .

[10]  Elisabeth Smela,et al.  Surprising Volume Change in PPy(DBS): An Atomic Force Microscopy Study , 1999 .

[11]  Jerald D. Kralik,et al.  Chronic, multisite, multielectrode recordings in macaque monkeys , 2003, Proceedings of the National Academy of Sciences of the United States of America.

[12]  E. Smela,et al.  Controlled Folding of Micrometer-Size Structures , 1995, Science.

[13]  David C. Martin,et al.  Polymerization of the conducting polymer poly(3,4-ethylenedioxythiophene) (PEDOT) around living neural cells. , 2007, Biomaterials.

[14]  I. Efimov,et al.  Time-scale- and temperature-dependent mechanical properties of viscoelastic poly(3,4-ethylenedioxythiophene) films. , 2005, Journal of the American Chemical Society.

[15]  David C. Martin,et al.  Electrochemical deposition and characterization of poly(3,4-ethylenedioxythiophene) on neural microelectrode arrays , 2003 .

[16]  J. Heinze,et al.  Electrochemical and spectroscopic characterization of polyalkylenedioxythiophenes , 1994 .

[17]  T. Gharbi,et al.  Culture of neural cells on polymers coated surfaces for biosensor applications. , 2005, Biosensors & bioelectronics.

[18]  R. J. Vetter,et al.  Silicon-substrate intracortical microelectrode arrays for long-term recording of neuronal spike activity in cerebral cortex , 2003, IEEE Transactions on Neural Systems and Rehabilitation Engineering.

[19]  R. Normann,et al.  Chronic recording capability of the Utah Intracortical Electrode Array in cat sensory cortex , 1998, Journal of Neuroscience Methods.

[20]  C. Schmidt,et al.  Micropatterned Polypyrrole: A Combination of Electrical and Topographical Characteristics for the Stimulation of Cells , 2007, Advanced functional materials.

[21]  D. Robinson,et al.  The electrical properties of metal microelectrodes , 1968 .

[22]  D. Kipke,et al.  Long-term neural recording characteristics of wire microelectrode arrays implanted in cerebral cortex. , 1999, Brain research. Brain research protocols.

[23]  S. Retterer,et al.  Controlling cellular reactive responses around neural prosthetic devices using peripheral and local intervention strategies , 2003, IEEE Transactions on Neural Systems and Rehabilitation Engineering.

[24]  D. Edell,et al.  Factors influencing the biocompatibility of insertable silicon microshafts in cerebral cortex , 1992, IEEE Transactions on Biomedical Engineering.

[25]  Wilfred Chen,et al.  Reversible conversion of conducting polymer films from superhydrophobic to superhydrophilic. , 2005, Angewandte Chemie.

[26]  E. Smela.  Conjugated Polymer Actuators for Biomedical Applications , 2003 .

[27]  Christine E. Schmidt,et al.  Conducting polymers in biomedical engineering , 2007 .

[28]  David C. Martin,et al.  Chronic neural recordings using silicon microelectrode arrays electrochemically deposited with a poly(3,4-ethylenedioxythiophene) (PEDOT) film , 2006, Journal of neural engineering.

[29]  Kip A Ludwig,et al.  Interfacing Conducting Polymer Nanotubes with the Central Nervous System: Chronic Neural Recording using Poly(3,4‐ethylenedioxythiophene) Nanotubes , 2009, Advanced materials.

[30]  S. Cogan.  Neural stimulation and recording electrodes. , 2008, Annual review of biomedical engineering.

[31]  Eva L Feldman,et al.  Aligned electrospun nanofibers specify the direction of dorsal root ganglia neurite growth. , 2007, Journal of biomedical materials research. Part A.

[32]  X. Cui,et al.  Poly (3,4-Ethylenedioxythiophene) for Chronic Neural Stimulation , 2007, IEEE Transactions on Neural Systems and Rehabilitation Engineering.

[33]  David C. Martin,et al.  The design of electrospun PLLA nanofiber scaffolds compatible with serum-free growth of primary motor and sensory neurons. , 2008, Acta biomaterialia.

[34]  R Langer,et al.  Stimulation of neurite outgrowth using an electrically conducting polymer. , 1997, Proceedings of the National Academy of Sciences of the United States of America.

[35]  Fen Chen,et al.  Evaluation of biocompatibility of polypyrrole in vitro and in vivo. , 2004, Journal of biomedical materials research. Part A.

[36]  Jin-Ye Wang,et al.  Characterization of nanostructure and cell compatibility of polyaniline films with different dopant acids. , 2008, The journal of physical chemistry. B.

[37]  R. Baughman.  Conducting polymer artificial muscles , 1996 .

[38]  G. Wallace,et al.  Use of Ionic Liquids for π-Conjugated Polymer Electrochemical Devices , 2002, Science.

[39]  Daryl R. Kipke,et al.  Voltage pulses change neural interface properties and improve unit recordings with chronically implanted microelectrodes , 2006, IEEE Transactions on Biomedical Engineering.

[40]  John R. Reynolds,et al.  Conjugated Polymers : Theory, Synthesis, Properties, and Characterization , 2006 .

[41]  Jon A. Mukand,et al.  Neuronal ensemble control of prosthetic devices by a human with tetraplegia , 2006, Nature.

[42]  R. Rosenfeld.  Nature , 2009, Otolaryngology--head and neck surgery : official journal of American Academy of Otolaryngology-Head and Neck Surgery.

[43]  D. Hubel.  Tungsten Microelectrode for Recording from Single Units. , 1957, Science.

[44]  P. Tresco,et al.  Response of brain tissue to chronically implanted neural electrodes , 2005, Journal of Neuroscience Methods.

[45]  J N Turner,et al.  Selective adhesion of astrocytes to surfaces modified with immobilized peptides. , 2002, Biomaterials.

[46]  William R. Stauffer,et al.  Polypyrrole doped with 2 peptide sequences from laminin. , 2006, Biomaterials.

[47]  Ravi V Bellamkonda,et al.  The role of aligned polymer fiber-based constructs in the bridging of long peripheral nerve gaps. , 2008, Biomaterials.

[48]  Ze Zhang,et al.  Electrically conductive biodegradable polymer composite for nerve regeneration: electricity-stimulated neurite outgrowth and axon regeneration. , 2007, Artificial organs.

[49]  Akiyoshi Shimada,et al.  Ion conducting polymer microelectrodes for interfacing with neural networks , 2007, Journal of Neuroscience Methods.

[50]  David C. Martin,et al.  Experimental and theoretical characterization of implantable neural microelectrodes modified with conducting polymer nanotubes. , 2008, Biomaterials.

[51]  M. Abidian,et al.  Conducting‐Polymer Nanotubes for Controlled Drug Release , 2006, Advanced materials.

[52]  C. Alemán,et al.  Cellular adhesion, proliferation and viability on conducting polymer substrates. , 2008, Macromolecular bioscience.

[53]  F. Jonas,et al.  Poly(alkylenedioxythiophene)s—new, very stable conducting polymers , 1992 .

[54]  J. Reynolds,et al.  Electrochemistry of Poly(3,4‐alkylenedioxythiophene) Derivatives , 2003 .

[55]  M. Berggren,et al.  Electronic control of Ca2+ signalling in neuronal cells using an organic electronic ion pump. , 2007, Nature materials.

[56]  G. Wallace,et al.  Conducting polymers for neural interfaces: challenges in developing an effective long-term implant. , 2008, Biomaterials.

[57]  Paul M. George,et al.  Fabrication and biocompatibility of polypyrrole implants suitable for neural prosthetics. , 2005, Biomaterials.