Double-Electrode Gas Metal Arc Welding, referred to as DE-GMAW, is a novel process which decouples the melting current into base metal current and bypass current by adding a bypass torch to a conventional GMAW system to establish a bypass arc. This makes it possible to increase the melting current while the base metal current still be controlled at a desired level. Experiments have been done to find the conditions which can assure a stable bypass arc be established/maintained between the welding wire and the bypass torch. To control the base metal current at the desired level, a group of power resistors is added in the bypass loop. The resistance of the power resistor group is adjusted real-time by changing the combination of the resistors and the change in the resistance results in a change in the bypass current thus a change in the base metal current. A model has been developed to correlate the change of the resistance needed to achieve the desired base metal current to the deviation of the base metal current from its desired level. * Corresponding author, email: ymzhang@engr.uky.edu 2 Experiments demonstrated that the developed control system can adjust the bypass current in a large range to maintain the base metal current at the desired levels.
[1]
Thomas W. Eagar,et al.
Analysis of metal transfer in gas metal arc welding
,
1993
.
[2]
Li Chun-xu.
Progress in variable polarity plasma arc welding
,
2004
.
[3]
John Eric Talkington,et al.
Variable polarity gas metal arc welding
,
1998
.
[4]
J. H. Waszink,et al.
Heat generation and heat flow in the filler metal in GMA welding
,
1982
.
[5]
S Tsushima,et al.
Tandem electrode AC‐MIG welding‐Development of AC‐MIG welding process (Report 4)
,
1994
.
[6]
Manabu Tanaka,et al.
Effects of torch configuration and welding current on weld bead formation in high speed tandem pulsed gas metal arc welding of steel sheets
,
2005
.