Failure-mechanism models for conductive-filament formation

This tutorial illustrates design and qualification situations where conductive filament formation, a failure mechanism that can occur in laminates, can affect product performance. Empirical models to design against this failure mechanism are presented in this paper. Examples illustrate the use of these models for design and qualification tests in electronic packaging. >

[1]  J. Lahti,et al.  The Characteristic Wearout Process in Epoxy-Glass Printed Circuits for High Density Electronic Packaging , 1979, 17th International Reliability Physics Symposium.

[2]  P. A. Engel,et al.  Failure models for mechanical wear modes and mechanisms , 1993 .

[3]  A. Dasgupta,et al.  Failure mechanism models for plastic deformation , 1992 .

[4]  P. J. Boddy,et al.  Accelerated Life Testing of Flexible Printed Circuits , 1976, 14th International Reliability Physics Symposium.

[5]  A. Dasgupta,et al.  Failure-mechanism models for excessive elastic deformation , 1992 .

[6]  C. W. Jennings.  Filament formation on printed wiring boards , 1975 .

[7]  J. Mitchell,et al.  Conductive Anodic Filaments in Reinforced Polymeric Dielectrics: Formation and Prevention , 1979, 17th International Reliability Physics Symposium.

[8]  P. Dumoulin,et al.  Metal Migrations Outside the Package During Accelerated Life Tests , 1982 .

[9]  A. Dasgupta,et al.  Mechanical design failure models for buckling , 1993 .

[10]  A. Dasgupta,et al.  Failure mechanism models for material aging due to interdiffusion , 1994 .

[11]  T. W. Griswold,et al.  Migratory Gold Resistive Shorts: Chemical Aspects of a Failure Mechanism , 1975, 13th International Reliability Physics Symposium.

[12]  Michael Pecht,et al.  Assessing time-to-failure due to conductive filament formation in multi-layer organic laminates , 1994 .

[13]  Alex Shumka,et al.  Migrated-Gold Resistive Shorts in Microcircuits , 1975, 13th International Reliability Physics Symposium.

[14]  A. Dasgupta,et al.  Failure mechanism models for brittle fracture , 1992 .

[15]  Aristos Christou,et al.  Failure mechanism models for electromigration , 1994 .

[16]  S. J. Krumbein,et al.  Metallic electromigration phenomena , 1988 .

[17]  T. L. Welsher,et al.  CAF in Composite Printed-Circuit Substrates: Characterization, Modeling and a Resistant Material , 1980, 18th International Reliability Physics Symposium.

[18]  A. Dasgupta,et al.  Failure-mechanism models for creep and creep rupture , 1993 .

[19]  M. Pecht,et al.  Material failure mechanisms and damage models , 1991 .

[20]  V. Tierney,et al.  The Nature and Rate of Creepage of Copper Sulfide Tarnish Films over Gold , 1981 .

[21]  G. T. Kohman,et al.  Silver migration in electrical insulation , 1955 .

[22]  A. Dasgupta,et al.  Failure mechanism models for cyclic fatigue , 1993 .