Vibration Durability Comparison of Sn37Pb vs SnAgCu Solders

In this paper, the vibration durability of SnAgCu (SAC) solders is compared to that of SnPb solder, using selected surface mount technology (SMT) interconnects. A time-domain approach, reported in the literature [1], was adopted for this study. Vibration durability tests under random excitation (between 10 Hz & 500 Hz) were conducted for both SAC and SnPb SMT boards. The test assembly consists of daisy-chained components, to facilitate real-time failure monitoring. Step-stress tests were conducted by increasing the RMS excitation levels from 7G to 14G in out of plane direction. The test was continued until most of the components on the board failed. In general, the SAC solders were found to have lower fatigue durability than the SnPb solder, under the vibration excitation levels applied in this study. This result is consistent with results in the literature from mechanical cycling studies, repetitive mechanical shock studies [2] and vibration studies [3] [4]. Destructive failure analysis (cross-sectioning, polishing and microscopy) was used to confirm that the failure was by solder fatigue. Durability model constants were estimated for a generalized Coffin-Manson strain-life fatigue model [5], for both SnPb and SAC solders© 2006 ASME

[1]  K. Upadhyayula,et al.  An incremental damage superposition approach for surface mount electronic interconnect durability under combined temperature and vibration environments , 1999 .

[2]  A. Dasgupta,et al.  Isothermal Mechanical Durability of Three Selected PB-Free Solders: Sn3.9Ag0.6Cu, Sn3.5Ag, and Sn0.7Cu , 2005 .

[3]  J. Lau,et al.  Solder Joint Reliability of Surface Mount Connectors , 1993 .

[4]  J. H. Lau,et al.  Solder joint reliability of flip chip and plastic ball grid array assemblies under thermal, mechanical, and vibration conditions , 1995, Proceedings of 1995 Japan International Electronic Manufacturing Technology Symposium.

[5]  J. Lau,et al.  Solder Joint Reliability of Large Plastic Ball Grid Array Assemblies Under Bending, Twisting,and Vibration Conditions , 1996 .

[6]  A. Dasgupta,et al.  Guidelines for physics-of-failure based accelerated stress testing , 1998, Annual Reliability and Maintainability Symposium. 1998 Proceedings. International Symposium on Product Quality and Integrity.

[7]  J. H. Lau,et al.  Solder joint reliability of flip chip and plastic ball grid array assemblies under thermal, mechanical, and vibrational conditions , 1996 .

[8]  J. H. Lau,et al.  Shock and Vibration of Solder Bumped Flip Chip on Organic Coated Copper Boards , 1996 .

[9]  Michael Pecht,et al.  PWB solder joint life calculations under thermal and vibrational loading , 1991, Annual Reliability and Maintainability Symposium. 1991 Proceedings.

[10]  Fook Fah Yap,et al.  Reliability of PBGA assemblies under out-of-plane vibration excitations , 2002 .

[11]  A. Dasgupta,et al.  Stress Analysis of Surface-Mount Interconnections Due to Vibrational Loading , 1997 .

[12]  Abhijit Dasgupta,et al.  Estimating the Vibration Fatigue Life of Quad Leaded Surface Mount Components , 1993 .

[13]  K. Banerji,et al.  Constitutive relations for tin-based-solder joints , 1992, 1992 Proceedings 42nd Electronic Components & Technology Conference.