Iron distribution in silicon after solar cell processing: Synchrotron analysis and predictive modeling

The evolution during silicon solar cell processing of performance-limiting iron impurities is investigated with synchrotron-based x-ray fluorescence microscopy. We find that during industrial phosphorus diffusion, bulk precipitate dissolution is incomplete in wafers with high metal content, specifically ingot border material. Postdiffusion low-temperature annealing is not found to alter appreciably the size or spatial distribution of FeSi2 precipitates, although cell efficiency improves due to a decrease in iron interstitial concentration. Gettering simulations successfully model experiment results and suggest the efficacy of high- and low-temperature processing to reduce both precipitated and interstitial iron concentrations, respectively.

[1]  B. Lai,et al.  Retrograde Melting and Internal Liquid Gettering in Silicon , 2010, Advanced materials.

[2]  D. Borchert,et al.  Improvement of multicrystalline silicon solar cells by a low temperature anneal after emitter diffusion , 2011 .

[3]  Z. Liliental-Weber,et al.  Coarsening and phase transition of FeSi2 precipitates in Si , 1994 .

[4]  J.R. Davis,et al.  Impurities in silicon solar cells , 1980, IEEE Transactions on Electron Devices.

[5]  U. Gösele,et al.  Modeling of gettering of precipitated impurities from Si for carrier lifetime improvement in solar cell applications , 1999 .

[6]  V. Mihailetchi,et al.  Effect of iron in silicon feedstock on p- and n-type multicrystalline silicon solar cells , 2008 .

[7]  A. Luque,et al.  Study of Internal versus External Gettering of Iron during Slow Cooling Processes for Silicon Solar Cell Fabrication , 2009 .

[8]  Antonio Luque,et al.  Acceptable contamination levels in solar grade silicon: From feedstock to solar cell , 2009 .

[9]  M. Pickett,et al.  Metal precipitation at grain boundaries in silicon: Dependence on grain boundary character and dislocation decoration , 2006 .

[10]  Matthew D. Pickett,et al.  Iron point defect reduction in multicrystalline silicon solar cells , 2008 .

[11]  K. Wambach,et al.  Precipitates and hydrogen passivation at crystal defects in n- and p-type multicrystalline silicon , 2007 .

[12]  A. Holt,et al.  Origin of the low carrier lifetime edge zone in multicrystalline PV silicon , 2009 .

[13]  L. J. Geerligs,et al.  Improved phosphorous gettering of multicrystalline silicon , 2006 .

[14]  Michael Seibt,et al.  Gettering in silicon photovoltaics: current state and future perspectives , 2006 .

[15]  D. Macdonald,et al.  Transition-metal profiles in a multicrystalline silicon ingot , 2005 .