Whereas a prior conception of glass dissolution assumed a relatively rapid initial dissolution which then slowed to a smaller, fairly constant longer-term rate, some recent work suggests that these two stages are followed by a third phase of dissolution, in which the dissolution rate is accelerated with respect to what had previously been thought of as the final long-term rate. The goals of the present study are to compile experimental data which may have a bearing on this phenomena, and to provide an initial assessment of these data. The Savannah River Technology Center (SRTC) is contracted to develop glass formulation models for vitrification of Hanford low-level waste (LLW), in support of the Hanford Tank Waste Remediation System Technology Development Program. The phenomenon of an increase in corrosion rate, following a period characterized by a low corrosion rate, has been observed by a number of researchers on a number of waste glass compositions. Despite inherent ambiguities arising from SA/V (glass surface area to solution volume ratio) and other effects, valid comparisons can be made in which accelerated corrosion was observed in one test, but not in another. Some glass compositions do not appear to attain a plateau region; it may be that the observation of continued, non-negligible corrosion in these glasses represents a passage from the initial rate to the accelerated rate. The long-term corrosion is a function of the interaction between the glass and its environment, including the leaching solution and the surrounding materials. Reaction path modeling and stability field considerations have been used with some success to predict the changes in corrosion rate over time, due to these interactions. The accelerated corrosion phenomenon highlights the need for such integrated corrosion modeling and the scenario-specific nature of a particular glass composition`s durability.
[1]
I. Pegg,et al.
A glass dissolution model for the effects of S/V on leachate pH☆
,
1994
.
[2]
William L. Ebert,et al.
A comparison of glass reaction at high and low glass surface/solution volume
,
1993
.
[3]
C. R. Bradley,et al.
Long-term comparison of dissolution behavior between fully radioactive and simulated nuclear waste glasses
,
1993
.
[4]
C. R. Bradley,et al.
ACCELERATED GLASS REACTION UNDER PCT CONDITIONS
,
1992
.
[5]
W. Ebert,et al.
Modeling Surface Area to Volume Effects on Borosilicate Glass Dissolution
,
1992
.
[6]
A. Barkatt,et al.
Leach Rate Excursions in Borosilicate Glasses: Effects of Glass and Leachant Composition
,
1990
.
[7]
W. Ebert,et al.
The reaction of synthetic nuclear waste glass in steam and hydrothermal solution
,
1989
.
[8]
P. B. Macedo,et al.
Effects of Surface Area-to-Solution Volume Ratio on Chemical Durability of Nuclear Waste Glasses
,
1989
.
[9]
N. Godon,et al.
R7T7 Nuclear Waste Glass Behavior in Moist Clay: Role of the Clay Mass/Glass Surface Area Ratio
,
1989
.
[10]
P. Van Iseghem,et al.
The Long-Term Corrosion and Modelling of Two Simulated Belgian Reference High-Level Waste Glasses
,
1987
.
[11]
J. W. Shade,et al.
Effect of high surface area to solution volume ratios on waste glass leaching
,
1986
.