Studies on sulfonic acid functionalized hollow silica spheres/Nafion® composite proton exchange membranes

In this work, sulfonic acid functionalized hollow silica spheres (SAFHSS)/Nafion® composite membranes were prepared by a recasting procedure. The influences of temperature on water uptake, swelling degree, and proton conductivity of the composite membranes were studied. In comparison with the pure recast Nafion® membrane, it was found that water uptake of composite membranes increased with increasing SAFHSS loading at all temperature studied. The swelling degree of SAFHSS/Nafion® composite membranes with 10∼15 wt % SAFHSS loading was lower than that of the pure recast Nafion® at all temperatures in the study. The proton conductivity of SAFHSS/Nafion® composite membranes was constantly higher than that of the pure recast Nafion® at all temperatures (50∼130 °C). In a range from 50 to 130 °C, the highest conductivity of composite membranes was obtained when 10 wt % SAFHSS was loaded. The maximum conductivity reached 0.1 S cm−1 at 100% relative humidity and 100 °C, even the temperature reached to 130 °C, the conductivity of the composite membranes with 10 wt % SAFHSS was still as high as 4.4 × 10−2 S cm−1 at 100% relative humidity, whereas the conductivity of the pure recast Nafion® was only 2.2 × 10−3 S cm−1. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 2647–2655, 2009

[1]  Hongfeng Xu,et al.  Hybrid Nafion–inorganic oxides membrane doped with heteropolyacids for high temperature operation of proton exchange membrane fuel cell , 2006 .

[2]  R. Marschall,et al.  Ordered Functionalized Silica Materials with High Proton Conductivity , 2007 .

[3]  Nanwen Li,et al.  Synthesis and properties of novel polyimides from sulfonated binaphthalene dianhydride for proton exchange membranes , 2008 .

[4]  D. Yan,et al.  Synthesis and characterization of thermally stable sulfonated polybenzimidazoles obtained from 3,3′‐disulfonyl‐4,4′‐dicarboxyldiphenylsulfone , 2005 .

[5]  S. Nunes,et al.  Sulfonated silica‐based electrolyte nanocomposite membranes , 2006 .

[6]  Robert B. Moore,et al.  TGA–FTi.r. investigation of the thermal degradation of Nafion® and Nafion®/[silicon oxide]-based nanocomposites , 1998 .

[7]  G. Robertson,et al.  Direct copolymerization of sulfonated poly(phthalazinone arylene ether)s for proton‐exchange‐membrane materials , 2003 .

[8]  L. Hong,et al.  Proton-conducting polymer membrane based on sulfonated polystyrene microspheres and an amphiphilic polymer blend , 2000 .

[9]  A. Eisenberg,et al.  Effect of ion placement and structure on properties of plasticized polyelectrolytes , 1977 .

[10]  A. Morin,et al.  Advanced Mesostructured Hybrid Silica−Nafion Membranes for High-Performance PEM Fuel Cell , 2008 .

[11]  Antonino S. Aricò,et al.  Nafion–TiO2 composite DMFC membranes: physico-chemical properties of the filler versus electrochemical performance , 2005 .

[12]  C. Ma,et al.  High proton-conducting Nafion®/–SO3H functionalized mesoporous silica composite membranes , 2007 .

[13]  J. Caro,et al.  Proton conductivity of sulfonic acid functionalised mesoporous materials , 2007 .

[14]  Y. Shul,et al.  Sulfonic-functionalized heteropolyacid-silica nanoparticles for high temperature operation of a direct methanol fuel cell , 2006 .

[15]  R. Savinell,et al.  Evaluation of a Sol-Gel Derived Nafion/Silica Hybrid Membrane for Polymer Electrolyte Membrane Fuel Cell Applications: II. Methanol Uptake and Methanol Permeability , 2001 .

[16]  D. Wan,et al.  A Facile Method for the Fabrication of Thiol-Functionalized Hollow Silica Spheres , 2008 .

[17]  Romuald Bogoczek,et al.  Studies on the thermal stability of the perfluorinated cation-exchange membrane Nafion-417 , 1988 .

[18]  James M. Fenton,et al.  Composite silica/Nafion® membranes prepared by tetraethylorthosilicate sol-gel reaction and solution casting for direct methanol fuel cells , 2006 .

[19]  Hyuk Chang,et al.  Nanocomposite membranes of surface-sulfonated titanate and Nafion® for direct methanol fuel cells , 2006 .

[20]  J. Caro,et al.  New proton conducting hybrid membranes for HT-PEMFC systems based on polysiloxanes and SO3H-functionalized mesoporous Si-MCM-41 particles , 2008 .

[21]  Min-Hsing Chang,et al.  Analysis of membraneless fuel cell using laminar flow in a Y-shaped microchannel , 2006 .

[22]  Joseph M. Norbeck,et al.  Nafion-bifunctional silica composite proton conductive membranes , 2002 .

[23]  Prabhuram Joghee,et al.  Preparation and characterization of hybrid Nafion–silica membrane doped with phosphotungstic acid for high temperature operation of proton exchange membrane fuel cells , 2004 .

[24]  K. Friedrich,et al.  Transport properties of ionomer composite membranes for direct methanol fuel cells , 2002 .

[25]  Itaru Honma,et al.  High Temperature Proton Conducting Organic/Inorganic Nanohybrids for Polymer Electrolyte Membrane Part II , 2002 .

[26]  Suzana P. Nunes,et al.  Inorganic modification of proton conductive polymer membranes for direct methanol fuel cells , 2002 .

[27]  M. Pina,et al.  Conductivity in zeolite-polymer composite membranes for PEMFCs , 2007 .

[28]  V. Antonucci,et al.  Hybrid Nafion-silica membranes doped with heteropolyacids for application in direct methanol fuel cells , 2001 .

[29]  G. Gohil,et al.  Sulfonated poly(ether ether ketone)/polyaniline composite proton-exchange membrane , 2006 .

[30]  I. Honma,et al.  Amphiphilic Organic/Inorganic Nanohybrid Macromolecules for Intermediate-Temperature Proton Conducting Electrolyte Membranes , 2002 .

[31]  Ronald K.A.M. Mallant.  PEMFC systems: the need for high temperature polymers as a consequence of PEMFC water and heat management , 2003 .

[32]  V. Antonucci,et al.  Influence of the acid-base characteristics of inorganic fillers on the high temperature performance of composite membranes in direct methanol fuel cells , 2003 .

[33]  H. Pu,et al.  Preparation and properties of Nafion®/hollow silica spheres composite membranes , 2008 .

[34]  H. Galiano,et al.  Nafion®/clay-SO3H membrane for proton exchange membrane fuel cell application , 2006 .

[35]  Chang Houn Rhee,et al.  Nafion/Sulfonated Montmorillonite Composite: A New Concept Electrolyte Membrane for Direct Methanol Fuel Cells , 2005 .

[36]  R. Jerome,et al.  Impact of acid containing montmorillonite on the properties of Nafion® membranes , 2005 .