Fatigue behavior and design of welded tubular T-joints with CHS brace and concrete-filled chord

Abstract Concrete-filled welded tubular structures have been increasingly used in large-span constructions such as truss bridges where fatigue failure is always a critical issue that should be focused on. This paper deals with fatigue behavior of CHS-CFSHS T-joints, which are made up of circular hollow section (CHS) braces and concrete-filled square hollow section (CFSHS) chords. Experimental results on stress concentration factor (SCF) were briefly summarized. Fatigue tests were conducted under cyclic tensile force in the brace, so that cracking patterns, failure modes and fatigue data of such joints were recorded. The tested CHS-CFSHS T-joints suffered from one of the following three failure modes: (i) brace-90°-side failure, (ii) chord-90°-side failure, (iii) chord-0°-side failure. Based on the fatigue data in terms of hot spot stress range ( S r,hs ) versus number of cycles ( N ), fatigue design S r,hs -N curves were determined using the deterministic and least-squares methods, respectively. It was found that most of the existing S r,hs -N curves are unsafe for fatigue design of CHS-CFSHS T-joints, except for the X´ S r,hs -N curve recommended by American Petroleum Institute [32] and American Welding Society [36]. In addition, the fatigue data of the CHS-CFSHS T-joints were found comparable with CHS-CFCHS T-joints (T-joints with CHS brace and concrete-filled CHS chord), hence a new fatigue design S r,hs -N curve was proposed for the both types of concrete-filled joints. A comparison between CHS-CFSHS T-joints and empty CHS-SHS T-joints showed that CHS-CFSHS T-joints generally have better fatigue behavior compared to their empty counterparts except for the case of extremely large ratio of brace diameter to chord width ( β ).

[1]  Fidelis R Mashiri,et al.  Stress-Concentration Factors in Circular Hollow Section and Square Hollow Section T-Connections: Experiments, Finite-Element Analysis, and Formulas , 2013 .

[2]  Xudong Qian,et al.  Fatigue and residual strength of concrete-filled tubular X-joints with full capacity welds , 2014 .

[3]  Kim Wallin,et al.  The probability of success using deterministic reliability , 1999 .

[4]  Xiao Ling Zhao,et al.  Experimental comparison in hot spot stress between CFCHS and CHS K-joints with gap , 2008 .

[5]  Fidelis R Mashiri,et al.  Static and fatigue design of CHS-to-RHS welded connections using a branch conversion method , 2007 .

[6]  Lichun Bian,et al.  Fatigue strength and stress concentration factors of CHS-to-RHS T-joints , 2003 .

[7]  Jeffrey A. Packer.  Concrete-Filled HSS Connections , 1995 .

[8]  Y. Sakai,et al.  Experiments on concrete filled and reinforced tubular K-joints of truss girder , 2004 .

[9]  Xiao Ling Zhao,et al.  Stress intensity factors of surface cracks in welded T-joints between CHS brace and concrete-filled CHS chord , 2008 .

[10]  Fidelis R Mashiri,et al.  Fatigue behaviour of welded thin-walled T-joints between circular and square hollow sections , 2006 .

[11]  L. Tong,et al.  Fatigue tests and design of diamond bird-beak SHS T-joints under axial loading in brace , 2016 .

[13]  Ju Chen,et al.  Experiment investigation of stress concentration factor of concrete-filled tubular T joints , 2010 .

[14]  Yoo Sang Choo,et al.  Stress intensity factor for a tubular T-joint with grouted chord , 2012 .

[15]  Fidelis R Mashiri,et al.  Fatigue Behavior of Welded T-Joints with a CHS Brace and CFCHS Chord under Axial Loading in the Brace , 2013 .

[16]  Fei Xu,et al.  Experimental investigation of SCF distribution for thin-walled concrete-filled CHS joints under axial tension loading , 2015 .

[17]  X. Zhao,et al.  Square hollow section (SHS) T-joints with concrete-filled chords subjected to in-plane fatigue loading in the brace , 2010 .

[18]  Young-Jin Kim,et al.  Stress concentration factors of N-joints of concrete-filled tubes subjected to axial loads , 2014 .

[19]  Fidelis R Mashiri,et al.  STRESS CONCENTRATION FACTORS AND FATIGUE FAILURE OF WELDED T-CONNECTIONS IN CIRCULAR HOLLOW SECTIONS UNDER IN-PLANE BENDING , 2004 .

[20]  Lin-Hai Han,et al.  Developments and advanced applications of concrete-filled steel tubular (CFST) structures: Members , 2014 .

[21]  Stig Berge,et al.  Fatigue Behavior of T-Joints: Square Chords and Circular Braces , 1998 .

[22]  Fidelis R Mashiri,et al.  Stress concentration factors and fatigue behaviour of welded thin-walled CHS¿SHS T-joints under in-plane bending , 2004 .