Indentation-induced interface delamination of a strong film on a ductile substrate

Abstract The objective of this work is to study indentation-induced delamination of a strong film from a ductile substrate. To this end, spherical indentation of an elastic–perfectly plastic substrate coated by an elastic thin film is simulated, with the interface being modeled by means of a cohesive surface. The constitutive law of the cohesive surface includes a coupled description of normal and tangential failure. Cracking of the coating itself is not included and residual stresses are ignored. Delamination initiation and growth are analyzed for several interfacial strengths and properties of the substrate. It is found that delamination occurs in a tangential mode rather than a normal one and is initiated at two to three times the contact radius. It is also demonstrated that the higher the interfacial strength, the higher the initial speed of propagation of the delamination and the lower the steady state speed. Indentation load vs. depth curves are obtained where, for relatively strong interfaces, the delamination initiation is imprinted on this curve as a kink.

[1]  A. Evans,et al.  The mechanics and physics of thin film decohesion and its measurement , 1996 .

[2]  Joshua R. Smith,et al.  Universal binding energy curves for metals and bimetallic interfaces , 1981 .

[3]  N. Moody,et al.  Quantitative adhesion measures of multilayer films: Part II. Indentation of W/Cu, W/W, Cr/W , 1999 .

[4]  Xiaopeng Xu,et al.  Void nucleation by inclusion debonding in a crystal matrix , 1993 .

[5]  M. Swain,et al.  Mechanical property characterization of thin films using spherical tipped indenters , 1994 .

[6]  Anthony G. Evans,et al.  Measurement of adherence of residually stressed thin films by indentation. I. Mechanics of interface delamination , 1984 .

[7]  Sarah V. Hainsworth,et al.  Using nanoindentation techniques for the characterization of coated systems: a critique , 1993 .

[8]  Anthony G. Evans,et al.  Spherical impression of thin elastic films on elastic–plastic substrates , 1999 .

[9]  Bunyamin Aksakal,et al.  A finite-element analysis of the indentation of an elastic-work hardening layered half-space by an elastic sphere , 1998 .

[10]  Viggo Tvergaard,et al.  VOID GROWTH AND FAILURE IN NOTCHED BARS , 1988 .

[11]  S. K. Biswas,et al.  A finite element study of the indentation mechanics of an adhesively bonded layered solid , 1998 .

[12]  T. Page,et al.  The effect of coating cracking on the indentation response of thin hard-coated systems , 1998 .

[13]  A. G. Evans,et al.  The mechanical performance of DLC films on steel substrates , 1998 .

[14]  A. Needleman,et al.  A tangent modulus method for rate dependent solids , 1984 .

[15]  Xiaopeng Xu,et al.  Numerical simulations of fast crack growth in brittle solids , 1994 .

[16]  Bharat Bhushan,et al.  Measurement of fracture toughness of ultra-thin amorphous carbon films , 1998 .