Crack propagation in concrete at very early ages

Surface defects and cracks in early-age concrete slabs have been observed to propagate under adverse conditions, impairing the performance and service life of these structures. However, the underlying mechanism of this form of crack propagation has remained largely unexplained, with very limited literature available. In this paper, simple yet sufficiently rigorous theoretical analyses of crack propagation in early-age concrete slabs, based on combined geotechnical engineering and fracture mechanics models, are presented. The results obtained clearly show how surface cracks can become unstable and propagate further, and either become stable again or develop through the full depth of the slab. They also convincingly demonstrate the roles of surface cracks and defects, pore moisture suctions and exposure conditions in this process. Importantly, the critical role of good construction practices in minimising this form of cracking is highlighted. These include proper compaction and effective curing as well as timely and adequate saw-cutting.

[1]  Peter F. Dux,et al.  Crack depths in desiccating plastic concrete , 2006 .

[2]  Alberto Carpinteri,et al.  Static and energetic fracture parameters for rocks and concretes , 1981 .

[3]  A. Hillerborg,et al.  Analysis of crack formation and crack growth in concrete by means of fracture mechanics and finite elements , 1976 .

[4]  Peter F. Dux,et al.  Plastic shrinkage cracking of concrete − roles of osmotic suction , 2011 .

[5]  Edwin G. Burdette,et al.  ELASTIC MODULUS, POISSON'S RATIO, AND COMPRESSIVE STRENGTH RELATIONSHIPS AT EARLY AGES , 1991 .

[6]  E. Orowan.  ENERGY CRITERIA OF FRACTURE , 1954 .

[7]  Sung-Hee Kim,et al.  Effect of temperature-induced load on airport concrete pavement behavior , 2014 .

[8]  F. Cohen Tenoudji,et al.  Mechanical properties of cement pastes and mortars at early ages: Evolution with time and degree of hydration , 1996 .

[9]  A. Janne Carlsson,et al.  Weight Functions and Stress Intensity Factor Solutions , 1991 .

[10]  Jan Olek,et al.  Mechanism of plastic shrinkage cracking in portland cement and portland cement-silica fume paste and mortar , 1990 .

[11]  Peter F. Dux,et al.  A Review of ACI Recommendations for Prevention of Plastic Cracking , 2005 .

[12]  Peter F. Dux,et al.  Tensile Properties of Early-Age Concrete , 2009 .

[13]  Konstantin Kovler,et al.  Testing system for determining the mechanical behaviour of early age concrete under restrained and free uniaxial shrinkage , 1994 .

[14]  A.Yu. Popov,et al.  Forced oscillations in imperfect and statically loaded shells , 1986 .

[15]  M. A. Crisfield,et al.  Snap‐through and snap‐back response in concrete structures and the dangers of under‐integration , 1986 .

[16]  Peter F. Dux,et al.  Suctions, fracture energy, and plastic cracking of cement mortar and concrete , 2005 .

[17]  Z. Bažant.  Concrete fracture models: testing and practice , 2002 .

[18]  P. E. Peterson,et al.  Fracture energy of concrete: Method of determination , 1980 .

[19]  J. Rice,et al.  Some remarks on elastic crack-tip stress fields , 1972 .

[20]  Peter F. Dux,et al.  Cracking of plastic concrete , 2003 .

[21]  L Ouldhammou,et al.  MECHANICAL PROPERTIES OF FRESH CONCRETE BEFORE SETTING , 1991 .

[22]  Luc Taerwe,et al.  Degree of hydration-based description of mechanical properties of early age concrete , 1996 .

[23]  H. Bueckner.  NOVEL PRINCIPLE FOR THE COMPUTATION OF STRESS INTENSITY FACTORS , 1970 .

[24]  J. Philip.  EVAPORATION, AND MOISTURE AND HEAT FIELDS IN THE SOIL , 1957 .

[25]  Alberto Carpinteri,et al.  Fracture of reinforced concrete: scale effects and snap-back instability , 1990 .

[26]  David J. Williams,et al.  Cracking in drying soils , 1992 .

[27]  P. Morris,et al.  Modification of dredged sediments to produce useful product by heating to high temperatures , 2005 .