Crack initiation and growth path under multiaxial fatigue loading in structural steels

Abstract In real engineering components and structures many accidental failures occur due to unexpected or additional loadings, such as additional bending or torsion. There are many factors influencing the fatigue crack paths, such as the material type (microstructure), structural geometry and loading path. It is widely believed that fatigue crack nucleation and early crack growth are caused by cyclic plasticity. This paper studies the effects of multiaxial loading paths on the cyclic deformation behaviour, crack initiation and crack path. Three types of structural steels are studied: Ck45, medium carbon steel, 42CrMo4, low alloy steel and the AISI 303 stainless steel. Four biaxial loading paths were applied in the tests to observe the effects of multiaxial loading paths on the additional hardening, fatigue crack initiation and crack propagation orientation. Fractographic analyses of the plane orientations of crack initiation and propagation were carried out by optical microscope and SEM approaches. It is shown that these materials have different crack orientations under the same loading path, due to their different cyclic plasticity behaviour and different sensitivity to non-proportional loading. Theoretical predictions of the damage plane were conducted using the critical plane approaches, either based on stress analysis or strain analysis (Findley, Smith–Watson–Topper, Fatemi–Socie, Wang–Brown–Miller, etc). Comparisons of the predicted crack orientation based on the critical plane approaches with the experimental observations for the wide range of loading paths and the three structural materials are shown and discussed. Results show the applicability of the critical plane approaches to predict the fatigue life and crack initial orientation in structural steels.

[1]  Hideo Takahashi,et al.  A STUDY ON FATIGUE CRACK GROWTH UNDER OUT‐OF‐PHASE COMBINED LOADINGS , 1997 .

[2]  David L. McDowell,et al.  A MICROCRACK GROWTH LAW FOR MULTIAXIAL FATIGUE , 1996 .

[3]  Harald Zenner,et al.  On the fatigue limit of ductile metals under complex multiaxial loading , 2000 .

[4]  Small crack growth in combined bending–torsion fatigue of A533B steel , 2001 .

[5]  K. N. Smith.  A Stress-Strain Function for the Fatigue of Metals , 1970 .

[6]  R. Hill.  Proceedings of the crack propagation symposium , 1963 .

[7]  Cetin Morris Sonsino,et al.  Assessment of the fatigue behaviour of welded aluminium joints under multiaxial spectrum loading by a critical plane approach , 2006 .

[8]  C. M. Sonsino,et al.  fatigue assessment of welded joints in AlMg 4.5Mn aluminium alloy (AA 5083) by local approaches , 1999 .

[9]  D. L. Mcdiarmid.  A GENERAL CRITERION FOR HIGH CYCLE MULTIAXIAL FATIGUE FAILURE , 1991 .

[10]  Darrell F. Socie,et al.  Constitutive modeling of metals under nonproportional cyclic loading , 1991 .

[11]  C. M. Sonsino.  Influence of load and deformation-controlled multiaxial tests on fatigue life to crack initiation , 2001 .

[12]  Marco Leite,et al.  Effects of non‐proportional loading paths on the orientation of fatigue crack path , 2005 .

[13]  A. Fatemi,et al.  A CRITICAL PLANE APPROACH TO MULTIAXIAL FATIGUE DAMAGE INCLUDING OUT‐OF‐PHASE LOADING , 1988 .

[14]  Cetin Morris Sonsino,et al.  Fatigue assessment of welded joints by local approaches Second edition , 2007 .

[15]  Ali Fatemi,et al.  Small Crack Growth in Multiaxial Fatigue , 1992 .

[16]  Tim Topper,et al.  The effect of bending overloads on torsional fatigue in normalized 1045 steel , 1999 .

[17]  Andrea Carpinteri,et al.  Handbook of fatigue crack propagation in metallic structures , 1994 .

[18]  I. Papadopoulos,et al.  Critical plane approaches in high-cycle fatigue : On the definition of the amplitude and mean value of the shear stress acting on the critical plane , 1998 .

[19]  Peter J. Bonacuse,et al.  Multiaxial fatigue and deformation : testing and prediction , 2000 .

[20]  Xu Chen,et al.  A critical plane-strain energy density criterion for multiaxial low-cycle fatigue life under non-proportional loading , 1999 .

[21]  W. Findley.  A Theory for the Effect of Mean Stress on Fatigue of Metals Under Combined Torsion and Axial Load or Bending , 1959 .

[22]  D. Socie,et al.  Nonproportional Low Cycle Fatigue Criterion for Type 304 Stainless Steel , 1995 .

[23]  F. Ellyin.  Fatigue Damage, Crack Growth and Life Prediction , 1996 .

[24]  Cetin Morris Sonsino,et al.  Present limitations in the assessment of components under multiaxial service loading , 2005 .

[25]  D. McDowell,et al.  Biaxial path dependence of deformation substructure of type 304 stainless steel , 1988 .

[26]  Chun H. Wang,et al.  Life Prediction Techniques for Variable Amplitude Multiaxial Fatigue—Part 1: Theories , 1996 .

[27]  Kc Liu,et al.  A Method Based on Virtual Strain-Energy Parameters for Multiaxial Fatigue Life Prediction , 1993 .