Advances in Research, Development, and Testing of Single Cells at Forschungszentrum Jülich

This paper presents an overview of the main advances in solid oxide fuel cells (SOFCs) research and development (R&D), measurement standardization, and quality assurance in SOFC testing at the Forschungszentrum Julich. These activities have resulted in both a significant improvement of the electrochemical performance and a better understanding of the electrochemical behavior of SOFCs. Research and development of SOFCs was mainly focused on two types of anode-supported cells, namely, those employing either La 0.65 Sr 0.3 MnO 3 (LSM) or La 0.58 Sr 0.4 Co 0.2 fe 0.8 O 3-δ (LSCF) cathode materials. In both cases the optimization of processing and microstructural parameters resulted in satisfactory power output and long-term stability at reduced operation temperatures. Standardization and quality assurance in SOFC testing was also addressed with the goal of producing consistent and reliable tests and measurement results. At present, under optimized experimental conditions, SOFCs with LSM or LSCF cathodes can deliver a power output of about 1.0 W/cm 2 and 1.9 W/cm 2 at 800°C (700 mV), respectively.

[1]  F. Tietz,et al.  Characterisation of Anode-Supported SOFCs with PSFC Cathode , 2009 .

[2]  J. Malzbender,et al.  Characterisation of Ni-cermets SOFCs with varying anode densities , 2007 .

[3]  Doris Sebold,et al.  Optimisation of processing and microstructural parameters of LSM cathodes to improve the electrochemical performance of anode-supported SOFCs , 2005 .

[4]  F. Ansart,et al.  Composition and porosity graded La2−xNiO4+δ (x≥0) interlayers for SOFC: Control of the microstructure via a sol–gel process , 2006 .

[5]  V. A. C. Haanappel,et al.  A review of standardising SOFC measurement and quality assurance at FZJ , 2007 .

[6]  A. Mai,et al.  Performance Improvement of (La,Sr)MnO3 and (La,Sr)(Co,Fe)O3-Type Anode-Supported SOFCs , 2006 .

[7]  Characterization of Anode-Supported Solid Oxide Fuel Cells With Nd2NiO4 Cathodes , 2009 .

[8]  Yong Wang,et al.  Preparation, thermal expansion, chemical compatibility, electrical conductivity and polarization of A2−αA′αMO4 (A = Pr, Sm; A′ = Sr; M = Mn, Ni; α = 0.3, 0.6) as a new cathode for SOFC , 2006 .

[9]  Andreas Mai,et al.  Electrode activation of anode-supported SOFCs with LSM- or LSCF-type cathodes , 2006 .

[10]  Andreas Mai,et al.  Ferrite-based perovskites as cathode materials for anode-supported solid oxide fuel cells. Part I. Variation of composition , 2005 .

[11]  Andreas Mai,et al.  Ferrite-based perovskites as cathode materials for anode-supported solid oxide fuel cells: Part II. Influence of the CGO interlayer , 2006 .

[12]  V. A. C. Haanappel,et al.  Quality Assurance and Solid Oxide Fuel Cell Testing at Forschungszentrum Juelich , 2007 .

[13]  J. Bassat,et al.  Oxygen diffusion and transport properties in non-stoichiometric Ln2 − xNiO4 + δ oxides , 2005 .

[14]  I. Vinke,et al.  Operation of anode-supported thin electrolyte film solid oxide fuel cells at 800°C and below , 1998 .

[15]  Izaak C. Vinke,et al.  Manufacturing of high performance solid oxide fuel cells (SOFCs) with atmospheric plasma spraying (APS) , 2007 .

[16]  F. Tietz,et al.  The influence of noble-metal-containing cathodes on the electrochemical performance of anode-supported SOFCs , 2004 .