The morphology of poly(terminal vinyl dimethicone-co-methyl methacrylate-co-n-butyl acrylate)/pigment composite film and its application in pigment printing of polyester fabric

In this study, a series of poly(terminal vinyl dimethicone-co-methyl methacrylate-co-n-butyl acrylate)/pigment composite particles (P(DMS-Acr)/PB CPs) were successfully prepared via miniemulsion polymerization and their latex film microstructures on were examined carefully using transmission electron microscopy (TEM), field emission scanning electron microscopy (FESEM), atomic force microscopy (AFM) and so on. Significant phase separation was observed after film formation, and the copper phthalocyanine blue (PB) particles tend to distribute in the polysiloxane island phase. After baking at 120 °C, the protrusions were generated. With increasing amount of vinyl terminated polydimethylsiloxane (ViPDMS) or baking time, the number of the protrusions became more and the appearance of the protrusions tends to be sharp. When the P(DMS-Acr)/PB CPs were applied in fabric printing, a continuous film was formed on the surface of the fabric at room temperature and therefore the gaps between yarns were blocked. However, the gaps in the fabric reappeared after baking at 120 °C, which could be attributed to the rapid flow of the polymer component. Finally, the fiber was coated with a layer of latex film containing a large number of mastoid structures, and the printed fabric could still retain the majority of the gaps between yarns and between fibers. Therefore, the printed fabric exhibited excellent performances such as good air permeability, softness, and rubbing fastness.

[1]  Qipeng Zhang,et al.  Divinyl‐terminated polysiloxane as an effective polyacrylates modifier for pigment printing: A study with different molecular weights and quantities , 2019, Journal of Applied Polymer Science.

[2]  H. Ni,et al.  New washing-free printing binder based on organosilicon-modified polyacrylate for polyester fabric printing of disperse dyes , 2018, Progress in Organic Coatings.

[3]  Hongyun Peng,et al.  Preparation of fluorescent pigment latex and its application on binder‐free printing of cotton fabrics , 2018 .

[4]  A. Han,et al.  Preparation and characterization of styrene-acrylic resin encapsulated C.I. Pigment Yellow 17 and charge control agent multicomponent particles , 2018, Journal of Coatings Technology and Research.

[5]  Liping Zhang,et al.  Preparation and characterization of aqueous phase self-dispersed CB/PSSS composites , 2017 .

[6]  S. Gunasekaran,et al.  Synthesis and applications of MANs/poly(MMA-co-BA) nanocomposite latex by miniemulsion polymerization , 2017, Royal Society Open Science.

[7]  Dongming Qi,et al.  Preparation of polymeric/inorganic nanocomposite particles in miniemulsions: I. Particle formation mechanism in systems stabilized with sodium dodecyl sulfate , 2017 .

[8]  M. Zohuriaan‐Mehr,et al.  Improving dirt pickup resistance in waterborne coatings using latex blends of acrylic/PDMS polymers , 2017 .

[9]  Yuqing Cai,et al.  The modification of cotton substrate using chitosan for improving its dyeability towards anionic microencapsulated nano-pigment particles , 2017 .

[10]  Rajkumar Ganugula,et al.  Synthesis of new rhodamine dyed copolymer nanodispersions for textiles-agglomeration and control with copolymer resins , 2016 .

[11]  M. Gradzielski,et al.  Development of self-curable hybrid pigment inks by miniemulsion polymerization for inkjet printing of cotton fabrics , 2016 .

[12]  A. Santos,et al.  Synthesis of Polymer/Silica Hybrid Latexes by Surfactant-Free RAFT-Mediated Emulsion Polymerization , 2016 .

[13]  F. Würthner,et al.  Organic Semiconductors based on Dyes and Color Pigments , 2016, Advanced materials.

[14]  X. Fei,et al.  Modified C.I. Pigment Red 170 with a core-shell structure: Preparation, characterization and computational study , 2016 .

[15]  RongZhan Liu,et al.  Utilizing cellulase as dispersant to prepare stable nano-pigment suspension and investigating its coloring performance on cotton fabrics , 2016 .

[16]  O. Hakeim,et al.  Preparation and characterization of UV curable-encapsulated phthalocyanine blue pigment , 2015 .

[17]  J. Kozakiewicz,et al.  Silicone-acrylic hybrid aqueous dispersions of core–shell particle structure and corresponding silicone-acrylic nanopowders designed for modification of powder coatings and plastics. Part III: Effect of modification with selected silicone-acrylic nanopowders on properties of polyurethane powder coat , 2015 .

[18]  Dongfang Wu,et al.  Synthesis and characterization of polyacrylate modified by polysiloxane latexes and films , 2014 .

[19]  J. Kozakiewicz,et al.  Silicone-acrylic hybrid aqueous dispersions of core–shell particle structure and corresponding silicone-acrylic nanopowders designed for modification of powder coatings and plastics. Part I – Effect of silicone resin composition on properties of dispersions and corresponding nanopowders , 2014 .

[20]  Xiaoyan Yuan,et al.  Preparation and evaluation of hydrophobic surfaces of polyacrylate-polydimethylsiloxane copolymers for anti-icing , 2013 .

[21]  Hongzheng Chen,et al.  CYM and RGB colored electronic inks based on silica-coated organic pigments for full-color electrophoretic displays , 2013 .

[22]  Serkan Baş,et al.  Optimization and comparison of polysiloxane acrylic hybrid latex synthesis methods , 2012, Journal of Polymer Research.

[23]  Jihu Wang,et al.  Preparation and characterization of carbon black‐polystyrene composite particles by high‐speed homogenization assisted suspension polymerization , 2012 .

[24]  Xiaoyu Li,et al.  Synthesis and characterization of core–shell polysilsesquioxane-poly(styrene-butyl acrylate-fluorinated acrylate) hybrid latex particles , 2012 .

[25]  Lingmin Yi,et al.  A Route to Modify Polymeric Pigment Dispersants with Polysiloxanes by Atom Transfer Radical Polymerization , 2012 .

[26]  Yiqi Yang,et al.  Synthesis of the Hydroxyl-Containing Poly(dimethyl siloxane) Modified Polyacrylate Core-Shell Latex and the Application as a Novel Binder for Pigment Printing of Fabric , 2011 .

[27]  Chunxia Wang,et al.  Properties of copper phthalocyanine blue encapsulated with a copolymer of styrene and maleic acid , 2010 .

[28]  F. Iskandar,et al.  Preparation and characterization of nanopigment‐poly(styrene‐co‐n‐butyl acrylate‐co‐methacrylic acid) composite particles by high speed homogenization‐assisted suspension polymerization , 2008 .

[29]  A. Meşe,et al.  Effect of storage duration on the hardness and tensile bond strength of silicone- and acrylic resin-based resilient denture liners to a processed denture base acrylic resin. , 2008, The Journal of prosthetic dentistry.

[30]  Brian S. Hawkett,et al.  Pigment encapsulation by emulsion polymerization using macro-RAFT copolymers. , 2008, Langmuir : the ACS journal of surfaces and colloids.

[31]  K. Landfester,et al.  Encapsulation of Organic Pigment Particles Via Miniemulsion Polymerization , 2007 .

[32]  M. Zielecka,et al.  Silicone-containing polymer matrices as protective coatings: Properties and applications , 2006 .

[33]  R. Schneider,et al.  Development of ecofriendly binders for pigment printing of all types of textile fabrics , 2006 .

[34]  Bojana Voncina,et al.  Properties of UV-cured pigment prints on textile fabric , 2006 .

[35]  J. Putaux,et al.  Silicone–polyacrylate composite latex particles. Particles formation and film properties , 2005 .

[36]  James E. Roberts,et al.  Incorporation of Alkoxysilanes into Model Latex Systems: Vinyl Copolymerization of Vinyltriethoxysilane and n-Butyl Acrylate , 2003 .

[37]  Lois E. Hamilton,et al.  Textile pigment printing binders prepared by modifying wheat gluten with methyl acrylate , 1998 .

[38]  Z. Hao,et al.  Some aspects of organic pigments , 1997 .