Ultrathin Seed-Layer for Tuning Density of ZnO Nanowire Arrays and Their Field Emission Characteristics

We report on how to tune the density of zinc oxide (ZnO) nanowire arrays in a wide range (more than 5 orders of magnitude) in a low temperature (80 °C) solution-phase growth process. A model based on the coexistence of nanowire growth and etching of the ultrathin ( 3.5 nm), the variation is very narrow, and if it is too thin (<1.5 nm), no nanowires can grow. In addition, the density variation was accompanied by the change of both diameter and height of the nanowires, which leads to a change in aspect ratio. Both changes in density and aspect ratio were found to obviously affect the field emission characteristics. It was demonstrated that optimal conditions can be found to grow ZnO nanowire films with better field emission characteristics.

[1]  Peidong Yang,et al.  Low-temperature wafer-scale production of ZnO nanowire arrays. , 2003, Angewandte Chemie.

[2]  Z. Dong,et al.  Growth mechanism of tubular ZnO formed in aqueous solution , 2006, Nanotechnology.

[3]  T. Tseng,et al.  Electrical characterizations of a controllable field emission triode based on low temperature synthesized ZnO nanowires , 2006 .

[4]  K. Kern,et al.  Tuning the Field Emission Properties of Patterned Carbon Nanotube Films , 2001 .

[5]  N. Xu,et al.  Field emission of one-dimensional micro- and nanostructures of zinc oxide , 2006 .

[6]  Zhong Lin Wang,et al.  In Situ Field Emission of Density‐Controlled ZnO Nanowire Arrays , 2007 .

[7]  L. Vayssieres.  Growth of Arrayed Nanorods and Nanowires of ZnO from Aqueous Solutions , 2003 .

[8]  László Forró,et al.  Field emission from single-wall carbon nanotube films , 1998 .

[9]  Sangwoo Lim,et al.  Effect of Seed Layer on the Growth of ZnO Nanorods , 2007 .

[10]  F. Ren,et al.  Low temperature (<100 °C) patterned growth of ZnO nanorod arrays on Si , 2007 .

[11]  Min Guo,et al.  Density-controlled hydrothermal growth of well-aligned ZnO nanorod arrays , 2007, Nanotechnology.

[12]  Zhong Lin Wang.  The new field of nanopiezotronics , 2007 .

[13]  D. Riley,et al.  Mechanism of ZnO nanotube growth by hydrothermal methods on ZnO film-coated Si substrates. , 2006, The journal of physical chemistry. B.

[14]  Bin Xiang,et al.  Efficient field emission from ZnO nanoneedle arrays , 2003 .

[15]  W. Graham,et al.  Atomic oxygen surface loss coefficient measurements in a capacitive/inductive radio-frequency plasma , 2002 .

[16]  J. Y. Lao,et al.  Field-emission studies on thin films of zinc oxide nanowires , 2003 .

[17]  Ningsheng Xu,et al.  Novel cold cathode materials and applications , 2005 .

[18]  Xiao Wei Sun,et al.  Field emission from zinc oxide nanopins , 2003 .