Study on Processing Technique in Engineering Tests of Mg-7.1Gd-4.6Y-1.3Nd-0.5Zr Alloy

Combined with the pre-test results, homogenization, plastic deformation, aging and other processes of Mg-7.1Gd-4.6Y-1.3Nd-0.5Zr (EW75) magnesium alloy was studied in engineering tests. The results show that in engineering test the large ingots (Φ500×800~900mm) of the EW75 alloy using two-stage homogenization treatment had perfect homogenization effect and no burnt structure. After multi-directional forging and extruded deformation, the homogenized residual second phase particles were fully broken, and the structure was refined and uniform. The peak aged craft was 230°C×6h, with the aging time increasing, the tensile strength and elongation remained unchanged, showing a strong anti-aging ability. The two-stage homogenization treatment + multi-directional forging + direct extrusion deformation + peak aging treatment was used to prepare a high performance EW75 alloy and at longitudinal direction its ultimate tensile strength, yield strength and elongation were 450MPa, 385MPa, 12.0% respectively.