The effects of nonhydrostatic compression and applied electric field on the electromechanical behavior of poled lead zirconate titanate 95/5–2Nb ceramic during the ferroelectric to antiferroelectric polymorphic transformation

We conducted hydrostatic compression and constant-stress-difference experiments, with and without an applied electric field, on poled, niobium-doped lead zirconate titanate ceramic. The objective was to quantify the effects of nonhydrostatic stress and electric field bias on electromechanical behavior of the ceramic during the ferroelectric, rhombohedral {r_arrow} antiferroelectric, orthorhombic phase transformation. Increasing stress difference (shear stress) decreases the mean stress at which the transformation occurs. Increasing shear stress also retards the rate of transformation, causing reductions in both the rate of charge release and peak voltage attained during depoling. Application of the electric field bias slightly increases the transformation pressure for poled ceramic. Previously, we showed that under nonhydrostatic stress, the transformation took place in {ital unpoled} ceramic when the maximum compressive stress equalled the hydrostatic pressure at which the transformation would otherwise occur. This simple stress criterion does not apply to poled ceramic. However, poled material has a preferred crystallographic orientation and mechanical anisotropy, whereas unpoled ceramic is isotropic. We present a qualitative model for the transformation under nonhydrostatic stress-related to that anisotropy, which resolves these seemingly disparate observations. {copyright} {ital 1999 Materials Research Society.}

[1]  D. Payne,et al.  The effect of external field symmetry on the antiferroelectric‐ferroelectric phase transformation , 1996 .

[2]  J. D. Keck,et al.  Further observations on the effects of nonhydrostatic compression on the FR1 → AO polymorphic phase transformation in niobiumdoped, lead-zirconate-titanate ceramic , 1994 .

[3]  R. D. Hardy,et al.  Event triggered data acquisition in the Rock Mechanics Laboratory , 1993 .

[4]  S. T. Montgomery,et al.  Hydrostatic and triaxial compression experiments on unpoled PZT 95/5–2Nb ceramic: The effects of shear stress on the F_R1 → A_O polymorphic phase transformation , 1992 .

[5]  E. Furman,et al.  Thermodynamic theory of the lead zirconate-titanate solid solution system, part I: Phenomenology , 1989 .

[6]  Leslie E. Cross,et al.  Thermodynamic theory of the lead zirconate-titanate solid solution system, part III: Curie constant and sixth-order polarization interaction dielectric stiffness coefficients , 1989 .

[7]  L. E. Cross,et al.  Thermodynamic theory of the lead zirconate-titanate solid solution system, part V: Theoretical calculations , 1989 .

[8]  E. Furman,et al.  Thermodynamic theory of the lead zirconate-titanate solid solution system, part II: Tricritical behavior , 1989 .

[9]  E. Furman,et al.  Thermodynamic theory of the lead zirconate-titanate solid solution system, part IV: Tilting of the oxygen octahedra , 1989 .

[10]  R. H. Dungan,et al.  Relation between Chemical, Mechanical, and Electrical Properties of Nb2O5‐Modified 95 Mol% PbZrO3‐5 Mol% PbTiO3 , 1985 .

[11]  I. J. Fritz Stress effects in two modified lead zirconate titanate ferroelectric ceramics , 1979 .

[12]  I. J. Fritz Uniaxial‐stress effects in a 95/5 lead zirconate titanate ceramic , 1978 .

[13]  J. D. Keck,et al.  Pressure-temperature phase diagrams for several modified lead zirconate ceramics , 1978 .

[14]  W. D. Means Stress and Strain: Basic Concepts of Continuum Mechanics for Geologists , 1976 .

[15]  L. Eyraud,et al.  Ferroelectric ceramics: Application to mechanical electrical energy conversion under shock compression , 1975 .

[16]  P. Lysne,et al.  Electric energy generation by shock compression of ferroelectric ceramics: Normal−mode response of PZT 95/5 , 1975 .

[17]  R. C. Fletcher Propagation of a coherent interface between two nonhydrostatically stressed crystals , 1973 .

[18]  M. Paterson,et al.  The α–β Inversion in quartz: A coherent phase transition under nonhydrostatic stress , 1969 .

[19]  S. R. Burlage Change of Elastic Constants through the Ferroelectric to Antiferroelectric Phase Transition in a Pb(Ti,Zr,Sn)O3 Ceramic , 1965 .