Residual stress effect on fatigue striation spacing in a cold-worked rivet hole

The residual stress effect due to cold-working is studied in relation to fatigue striation spacing. Cold-working introduces a compressive stress field around the hole reducing the tendency for fatigue cracks to initiate and grow under cyclic mechanical loading. It is known that fatigue lifetime assessment requires a detailed knowledge of the residual stress profile. X-ray diffraction and 3D finite element analysis (FEA) can be used to determine the residual stress profile. Scanning electron microscopy (SEM) measurements were performed for measuring the striation spacing.

[1]  J. Y. Mann,et al.  FATIGUE OF THICK‐SECTION COLD‐EXPANDED HOLES WITH AND WITHOUT CRACKS , 1989 .

[2]  Jp Gallagher,et al.  Proposed Fracture Mechanics Criteria to Select Mechanical Fasteners for Long Service Lives , 1974 .

[3]  A. Leon,et al.  Benefits of split mandrel coldworking , 1998 .

[4]  Manuel François,et al.  Residual stresses and crystallographic texture in hard-chromium electroplated coatings , 1997 .

[5]  Cgc Poussard,et al.  Effect of residual stress around cold worked holes on fracture under superimposed mechanical load , 1999 .

[6]  D. L. Ball,et al.  ELASTIC‐PLASTIC STRESS ANALYSIS OF COLD EXPANDED FASTENER HOLES , 1995 .

[7]  G. A. Webster,et al.  Residual stress distributions and their influence on fatigue lifetimes , 2001 .

[8]  Jaap Schijve,et al.  Fatigue of structures and materials , 2001 .

[9]  Jidong Kang,et al.  Three-Dimensional Finite Element Analysis of the Cold Expansion of Fastener Holes in Two Aluminum Alloys , 2002 .

[10]  A. F. GrandtJr..  Stress intensity factors for some through-cracked fastener holes , 1975 .

[11]  M. J. Pavier,et al.  Finite element modelling of the interaction of residual stress with mechanical load for a crack emanating from a cold worked fastener hole , 1998 .

[12]  M. Pavier,et al.  An assessment of residual-stress measurements around cold-worked holes , 1995 .

[13]  Cgc Poussard,et al.  A finite element simulation of the cold working process for fastener holes , 1997 .

[14]  Dl Ball,et al.  Experimental investigation on the effects of cold expansion of fastener holes , 1998 .

[15]  Guowanlin.  Elastic-plastic analysis of a finite sheet with a cold-worked hole , 1993 .

[16]  Pc Paris,et al.  Fracture Toughness and Slow-Stable Cracking , 1974 .

[17]  Cgc Poussard,et al.  Analytical and finite element predictions of residual stresses in cold worked fastener holes , 1995 .

[18]  A. F. Grandt,et al.  Stress intensity factors for some through-cracked fastener holes , 1975 .

[19]  Guo Wanlin.  Elastic-plastic analysis of a finite sheet with a cold-worked hole , 1993 .

[20]  L. Schwarmann.  On improving the fatigue performance of a double-shear lap joint , 1983 .

[21]  E. W O'Brien,et al.  Beneficial residual stress from the cold expansion of large holes in thick light alloy plate , 2000 .

[22]  G. Clark,et al.  MODELLING RESIDUAL STRESSES AND FATIGUE CRACK GROWTH AT COLD-EXPANDED FASTENER HOLES , 1991 .

[23]  M. H. Aliabadi.  Computer Methods and Experimental Measurements for Surface Treatment Effects , 1993 .