Micro-shear bond strength of different adhesives to human dental enamel.

UNLABELLED The aim of this study was to evaluate the micro-shear bond strength of 5 adhesive systems to enamel, one single-bottle acid-etch adhesive (O), two self-etching primers (P) and two all-in-one self-etching adhesives (S). METHOD Sixty premolar enamel surfaces (buccal or lingual) were ground flat with 400- and 600-grit SiC papers and randomly divided into 5 groups (n = 12), according to the adhesive system: SB2--Single Bond 2 (O); CSE--Clearfil SE Bond (P); ADS--AdheSE (P); PLP--Adper Prompt L-Pop (S); XE3--Xeno III (S). Tygon tubing (inner diameter of 0.8 mm) restricted the bonding area to obtain the resin composite (Z250) cylinders. After storage in distilled water at 37 degrees C for 24h and thermocycling, micro-shear testing was performed (crosshead speed of 0.5 mm/min). Data were submitted to one-way ANOVA and Tukey test (a = 5%). Samples were also subjected to stereomicroscopic and SEM evaluations after micro-shear testing. Mean bond strength values (MPa +/- SD) and the results of Tukey test were: SB2: 36.36 (+/- 3.34)a; ADS: 33.03 (17.83)a; XE3: 32.76 (+/- 5.61)a; CSE: 30.61 (+/- 6.68)a; PLP: 22.17 (+/- 6.05)b. Groups with the same letter were not statistically different. It can be concluded that no significant difference was there between SB2, ADS, XE3 and CSE, in spite of different etching patterns of these adhesives. Only PLP presented statistically lower bond strengths compared with others.

[1]  A. Feilzer,et al.  Bond efficacy and interface morphology of self-etching adhesives to ground enamel. , 2010, The journal of adhesive dentistry.

[2]  R. Braga,et al.  Adhesion to tooth structure: a critical review of "macro" test methods. , 2010, Dental materials : official publication of the Academy of Dental Materials.

[3]  V. Arana-Chavez,et al.  BOND STRENGTH AND MORPHOLOGY OF ENAMEL USING SELF-ETCHING ADHESIVE SYSTEMS WITH DIFFERENT ACIDITIES , 2009, Journal of applied oral science : revista FOB.

[4]  M. Burrow,et al.  Comparison of enamel and dentin microshear bond strengths of a two-step self-etching priming system with five all-in-one systems. , 2008, Operative dentistry.

[5]  Y. Talic,et al.  The effect of thermocycling on the adhesion of self-etching adhesives on dental enamel and dentin. , 2007, The journal of contemporary dental practice.

[6]  A. Feilzer,et al.  Fatigue testing of enamel bonds with self-etch and total-etch adhesive systems. , 2006, Dental materials : official publication of the Academy of Dental Materials.

[7]  D. Pashley,et al.  The microtensile bond strength of self-etching adhesives to ground enamel. , 2006, Operative dentistry.

[8]  A. Reis,et al.  Does the acidity of self-etching primers affect bond strength and surface morphology of enamel? , 2006, The journal of adhesive dentistry.

[9]  P. Lambrechts,et al.  Bond strength of a mild self-etch adhesive with and without prior acid-etching. , 2006, Journal of dentistry.

[10]  J. Perdigão,et al.  Enamel bond strengths of pairs of adhesives from the same manufacturer. , 2005, Operative dentistry.

[11]  J. Tagami,et al.  Micro-shear bond strength and morphological analysis of a self-etching primer adhesive system to fluorosed enamel. , 2005, Journal of dentistry.

[12]  M. A. Sinhoreti,et al.  SEM evaluation of contemporary self-etching primers applied to ground and unground enamel. , 2005, The journal of adhesive dentistry.

[13]  V. Arana-Chavez,et al.  Odontoblasts: the cells forming and maintaining dentine. , 2004, The international journal of biochemistry & cell biology.

[14]  Marcelo Giannini,et al.  Ultimate tensile strength of tooth structures. , 2004, Dental materials : official publication of the Academy of Dental Materials.

[15]  G. Schmalz,et al.  Bond strength of self-etching adhesives to dental hard tissues , 2002, Clinical Oral Investigations.

[16]  M. Burrow,et al.  Bond strength of two adhesive systems to primary and permanent enamel. , 2002, Operative dentistry.

[17]  F. Tay,et al.  Aggressiveness of contemporary self-etching adhesives. Part II: etching effects on unground enamel. , 2001, Dental materials : official publication of the Academy of Dental Materials.

[18]  A T Hara,et al.  Shear bond strength of hydrophilic adhesive systems to enamel. , 1999, American journal of dentistry.

[19]  T. Hayakawa,et al.  Influence of self-etching primer treatment on the adhesion of resin composite to polished dentin and enamel. , 1998, Dental materials : official publication of the Academy of Dental Materials.

[20]  P. Lambrechts,et al.  Effects of a self-etching primer on enamel shear bond strengths and SEM morphology. , 1997, American journal of dentistry.