Polymerization of propylene to syndiotactic polymer. III. Behaviour of the catalyst system VCl4‐Al(C2H5)2Cl in the presence of lewis bases

Polymerizations of propylene to syndiotactic polymer have been carried out in the presence of the catalyst system VCl4-Al(C2H5)2Cl-anisole. The data obtained have been related to those previously reported concerning the catalyst system, VCl4-Al(C2H5)2Cl. It was thus possible to propose a mechanism of formation of the catalytic complexes and to put forward or confirm some hypotheses on their constitution. A polymerization mechanism is also proposed that can justify both the type of stereoregularity of the polymer and the variation of steric regularity on varying the polymerization conditions. Propylen wurde mit dem Katalysatorsystem VCL4-Al(C2H5)2Cl-Anisol zu syndiotaktischem Polypropylen polymerisiert. Die Ergebnisse werden mit fruheren Versuehen verglichen, bei denen das binare System VCl4-Al(C2H5)2Cl verwendet wurde. Aus den erhaltenen Daten konnten ein Bildungsmechanismus und die mutmasliche Struktur des katalytisch wirksamen Komplexes abgeleitet werden. Ferner wird ein Polymerisationsmechanismus mus vorgeschlagen, der sowohl den Typ der Stereoregularitat als auch deren Anderung mit wechselnden Polymerisationsbedingungen erkart.