An elastic-plastic finite element analysis of crack initiation, stable crack growth, and instability

Studies have been conducted to develop efficient techniques to simulate crack extension and to examine various local and global fracture criteria. Of the considered criteria, the crack-tip-opening angle (CTOA) or displacement (CTOD) at a specified distance from the crack tip was shown to be most suited for modeling stable crack growth and instability during the fracture process. The results obtained in a number of studies show the necessity for studying different crack configurations when assessing the validity of any fracture criteria. One of the objectives of the present investigation is related to a critical evaluation of the CTOD growth criterion using an elastic-plastic finite element analysis under monotonic loading to failure. The analysis was found to predict three stages of crack growth behavior under monotonic loading to failure. Calculated CTOD values agreed well with experimental values for crack growth initiation.