Green composites. I. physical properties of ramie fibers for environment-friendly green composites

The surface topography, tensile properties, and thermal properties of ramie fibers were investigated as reinforcement for fully biodegradable and environmental-friendly ‘green’ composites. SEM micrographs of a longitudinal and cross-sectional view of a single ramie fiber showed a fibrillar structure and rough surface with irregular cross-section, which is considered to provide good interfacial adhesion with polymer resin in composites. An average tensile strength, Young’s modulus, and fracture strain of ramie fibers were measured to be 627 MPa, 31.8 GPa, and 2.7 %, respectively. The specific tensile properties of the ramie fiber calculated per unit density were found to be comparable to those of E-glass fibers. Ramie fibers exhibited good thermal stability after aging up to 160°C with no decrease in tensile strength or Young’s modulus. However, at temperatures higher than 160°C the tensile strength decreased significantly and its fracture behavior was also affected. The moisture content of the ramie fiber was 9.9%. These properties make ramie fibers suitable as reinforcement for ‘green’ composites. Also, the green composites can be fabricated at temperatures up to 160°C without reducing the fiber properties.

[1]  P. Cheremisinoff,et al.  Handbook of Engineering Polymeric Materials , 1997 .

[2]  J. Jog,et al.  Natural fiber polymer composites: A review , 1999 .

[3]  A. Netravali,et al.  Characterization of henequen fibers and the henequen fiber/poly(hydroxybutyrate-co-hydroxyvalerate) interface , 2001 .

[4]  P. Singer.  Editorial: Environmental R&D , 1984 .

[5]  M. Misra,et al.  Biofibres, biodegradable polymers and biocomposites: An overview , 2000 .

[6]  Anil N. Netravali,et al.  Mechanical and thermal properties of environment-friendly green composites made from pineapple leaf fibers and poly(hydroxybutyrate-co-valerate) resin , 1999 .

[7]  G. Thomas,et al.  Wood fibers as reinforcing fillers for polyolefins , 1984 .

[8]  C. Pavithran,et al.  Impact properties of sisal-glass hybrid laminates , 1991 .

[9]  A. Netravali,et al.  Characterization of ramie fiber/soy protein concentrate (SPC) resin interface , 2004 .

[10]  Andrzej K. Bledzki,et al.  Properties and modification methods for vegetable fibers for natural fiber composites , 1996 .

[11]  H. Wu,et al.  Weibull analysis of strength-length relationships in single Nicalon SiC fibres , 1992 .

[12]  M. Lewin.  Handbook of Fiber Chemistry , 2006 .

[13]  Li Shihong,et al.  A new kind of super-hybrid composite material for civil use - ramie fibre/Al , 1994 .

[14]  Anil N. Netravali,et al.  Characterization of stearic acid modified soy protein isolate resin and ramie fiber reinforced ‘green’ composites , 2005 .

[15]  Sabu Thomas,et al.  Tensile properties of short sisal fiber reinforced polystyrene composites , 1996 .

[16]  Sabu Thomas,et al.  A review on interface modification and characterization of natural fiber reinforced plastic composites , 2001 .

[17]  G. E. Myers,et al.  Thermal Degradation of Wood Fillers at the Melt-Processing Temperatures of Wood-Plastic Composites: Effects on Wood Mechanical Properties and Production of Voiatiles , 1993 .

[18]  Anil N. Netravali,et al.  Characterization of interfacial and mechanical properties of “green” composites with soy protein isolate and ramie fiber , 2002 .

[19]  B. Barkakaty.  Some structural aspects of sisal fibers , 1976 .

[20]  Anil N. Netravali,et al.  Interfacial and mechanical properties of environment-friendly “green” composites made from pineapple fibers and poly(hydroxybutyrate-co-valerate) resin , 1999 .

[21]  J. Valade,et al.  Use of wood fibers in thermoplastic composites , 1983 .

[22]  M. Misra,et al.  Studies on Jute Composites—A Literature Review , 1995 .

[23]  Martin P. Ansell,et al.  Properties of sisal-CNSL composites , 1992, Journal of Materials Science.

[24]  H. Bader,et al.  Influence of natural fibres on the mechanical properties of biodegradable polymers. , 1998 .

[25]  B. Chabert,et al.  Realization of Polypropylene/Sisal Fiber Composites by Reactive Extrusion , 1996 .

[26]  J. d’Almeida,et al.  Effect of Water Absorption on the Mechanical Properties of Sisal and Jute Fiber Composites , 1999 .

[27]  A. Błędzki,et al.  Composites reinforced with cellulose based fibres , 1999 .

[28]  P. Herrera-Franco,et al.  Physical and mechanical properties of henequen fibers , 1991 .

[29]  Roger M. Rowell,et al.  The Chemistry of solid wood , 1984 .

[30]  D. Fengel,et al.  A chemical and ultrastructural study of the Bamboo species Phyllostachys makinoi Hay , 1984, Wood Science and Technology.

[31]  M. Misra,et al.  Surface characterization of natural fibers; surface properties and the water up-take behavior of modified sisal and coir fibers , 2001 .

[32]  A. Netravali,et al.  Characterization of Phytagel® modified soy protein isolate resin and unidirectional flax yarn reinforced “green” composites , 2005 .

[33]  W. Davies.  The chemistry of milk , 1936 .

[34]  C. Joly,et al.  Interfaces in polyolefin/cellulosic fiber composites: Chemical coupling, morphology, correlation with adhesion and aging in moisture , 1998 .