Effect of multipass TIG welding on the corrosion resistance and microstructure of a super duplex stainless steel

This is a study of the effect of repetitive TIG (tungsten inert gas) welding passes, melting and remelting the same material volume on microstructure and corrosion resistance of 2507 (EN 1.4410) super duplex stainless steel. One to four weld passes were autogenously (no filler added) applied on a plate using two different arc energies and with pure argon shielding gas. Sensitization testing showed that multipass remelting resulted in significant loss of corrosion resistance of the weld metal, in base material next to the fusion boundary, and in a zone 1 to 4 mm from the fusion boundary. Metallography revealed the main reasons for sensitization to be a ferrite‐rich weld metal and precipitation of nitrides in the weld metal, and adjacent heat affected zone together with sigma phase formation at some distance from the fusion boundary. Corrosion properties cannot be significantly restored by a post weld heat treatment. Using filler metals with higher nickel contents and nitrogen containing shielding gases, are therefore, recommended. Welding with a higher heat input and fewer passes, in some cases, can also decrease the risk of formation of secondary phases and possible corrosion attack.

[1]  V. Hosseini,et al.  Nitrogen loss and effects on microstructure in multipass TIG welding of a super duplex stainless steel , 2016 .

[2]  L. Karlsson,et al.  Influence of multiple thermal cycles on microstructure of heat-affected zone in TIG-welded super duplex stainless steel , 2016, Welding in the World.

[3]  N. Llorca-Isern,et al.  Identification of sigma and chi phases in duplex stainless steels , 2016 .

[4]  M. Vignesh,et al.  Effect of optimal weld parameters in the microstructure and mechanical properties of autogeneous gas tungsten arc weldments of super-duplex stainless steel UNS S32750 , 2015 .

[5]  Yiming Jiang,et al.  Effect of a brief post-weld heat treatment on the microstructure evolution and pitting corrosion of laser beam welded UNS S31803 duplex stainless steel , 2012 .

[6]  Yong-Soo Park,et al.  Investigation of the localized corrosion associated with phase transformation of tube-to-tube sheet welds of hyper duplex stainless steel in acidified chloride environments , 2012 .

[7]  Ziying Zhang,et al.  Effect of post-weld heat treatment on microstructure evolution and pitting corrosion behavior of UNS S31803 duplex stainless steel welds , 2012 .

[8]  L. Karlsson,et al.  Low Energy Input Welding Of Duplex Stainless Steels , 2012, Welding in the World.

[9]  Alberto M. Gambaruto,et al.  Flow structures in cerebral aneurysms , 2012 .

[10]  Michael Rethmeier,et al.  Numerical calculation of residual stress development of multi-pass gas metal arc welding , 2012 .

[11]  Leif Welding Duplex Stainless Steels — A Review Of Current Recommendations , 2012, Welding in the World.

[12]  Zhiyu Wang,et al.  Influence of welding thermal cycles on microstructure and pitting corrosion resistance of 2304 duplex stainless steels , 2012 .

[13]  Zhiyu Wang,et al.  Annealing temperature effect on the pitting corrosion resistance of plasma arc welded joints of duplex stainless steel UNS S32304 in 1.0 M NaCl , 2011 .

[14]  A. Davoodi,et al.  Correlation between critical pitting temperature and degree of sensitisation on alloy 2205 duplex stainless steel , 2011 .

[15]  David Garrett A Corrosion Management and Applications Engineering Magazine from Outokumpu Welded Stainless Steel Tubes & Pipes vs. Seamless , 2011 .

[16]  C. García,et al.  Effect of ageing heat treatments on the microstructure and intergranular corrosion of powder metallurgy duplex stainless steels , 2010 .

[17]  Jin Li,et al.  Effect of annealing treatment on microstructure evolution and the associated corrosion behavior of a super-duplex stainless steel , 2010 .

[18]  Yiming Jiang,et al.  Effect of annealing temperature on the pitting corrosion resistance of super duplex stainless steel UNS S32750 , 2009 .

[19]  J. Pardal,et al.  Influence of microstructure on the corrosion resistance of the duplex stainless steel UNS S31803 , 2008 .

[20]  M. I. Barrena,et al.  The effect of N2 addition upon the MIG welding process of duplex steels , 2007 .

[21]  Jan Olsson,et al.  Duplex — A new generation of stainless steels for desalination plants , 2007 .

[22]  M. Pohl,et al.  Effect of intermetallic precipitations on the properties of duplex stainless steel , 2007 .

[23]  K. Saida,et al.  Prediction of Sigma Phase Precipitation in Super Duplex Stainless Steel Weldments , 2006 .

[24]  H. Wang Effect of Welding Variables on Cooling Rate and Pitting Corrosion Resistance in Super Duplex Stainless Weldments , 2005 .

[25]  S. Seshadri,et al.  Effect of weld metal chemistry and heat input on the structure and properties of duplex stainless steel welds , 2003 .

[26]  J. Lippold,et al.  The relationship between chromium nitride and secondary austenite precipitation in duplex stainless steels , 2003 .

[27]  Mariano Marcos,et al.  Influence of chemical composition on the pitting corrosion resistance of non-standard low-Ni high-Mn–N duplex stainless steels , 2003 .

[28]  J. Liao Nitride precipitation in weld HAZs of a duplex stainless steel , 2001 .

[29]  S. Wolynec,et al.  Evaluation of the low corrosion resistant phase formed during the sigma phase precipitation in duplex stainless steels , 1999 .

[30]  P. Uggowitzer,et al.  Partitioning of chromium and molybdenum in super duplex stainless steels with respect to nitrogen and nickel content , 1998 .

[31]  R. Gunn Duplex stainless steels : microstructure, properties and applications , 1997 .

[32]  A. Wilson,et al.  Influence of isothermal phase transformations on toughness and pitting corrosion of super duplex stainless steel SAF 2507 , 1993 .

[33]  R. Kelly,et al.  An Electrochemical Test for Detecting the Intergranular Corrosion Susceptibility of a Duplex Stainless Steel , 1986 .

[34]  Jan-Olof Andersson,et al.  The Thermo-Calc databank system☆ , 1985 .