A Case Study On Stabilization And Reuse Of Geopolymer-encapsulated Brown Coal Fly Ash

Fly ash disposal for coal power stations is an ongoing problem. This paper explores the use of a geopolymeric material to stabilize fly ash and reduce the leach rates of metals, and at the same time determine whether the stabilized material can be reused and recycled as value-added products. Fly ash from the Latrobe Valley, Victoria, Australia, was collected and stabilized in a geopolymer with a molar silica to alumina ratio of 3. Fly ash was collected from electrostatic precipitators [precipitator fly ash (PFA)] and ash disposal ponds [leached fly ash (LFA)] so that a comparison in results between the two types could be made. In terms of stabilization of selected heavy metals, PFA showed better trends towards reduction in leach rates, although for this fly ash the initial concentration of heavy metals is low. LFA showed better trends towards reduction in major elemental leach rates. Compressive strength tests were carried out to determine the potential of the material to be used as recycled products. A maximum compressive strength of 32 MPa was achieved with a PFA‐geopolymer combination, which shows that these materials can be recycled and reused. However, more research is still required to achieve greater compressive strengths. Scanning electron microscopy linked the leaching behaviour and compressive strength values with images that showed the fly ash particle‐geopolymer interaction. Materials cost estimation was conducted to determine the cost of materials required to stabilize and reuse fly ash geopolymers.

[1]  J. Deventer,et al.  The effect of ionic contaminants on the early-age properties of alkali-activated fly ash-based cements , 2002 .

[2]  J.S.J. van Deventer,et al.  The potential use of geopolymeric materials to immobilise toxic metals: Part II. Material and leaching characteristics , 1999 .

[3]  J.S.J. van Deventer,et al.  Factors affecting the immobilization of metals in geopolymerized flyash , 1998 .

[4]  J. Phair,et al.  Effect of the silicate activator pH on the microstructural characteristics of waste-based geopolymers , 2002 .

[5]  Ángel Palomo,et al.  Alkali-activated cementitous materials: Alternative matrices for the immobilisation of hazardous wastes Part I. Stabilisation of boron , 2003 .

[6]  J. Davidovits.  Geopolymers : inorganic polymeric new materials , 1991 .

[7]  Ramasubramania Iyer,et al.  Power station fly ash : a review of value-added utilization outside of the construction industry , 2001 .

[8]  K. MacKenzie,et al.  Synthesis and characterisation of materials based on inorganic polymers of alumina and silica: sodium polysialate polymers , 2000 .

[9]  J.S.J. van Deventer,et al.  The potential use of geopolymeric materials to immobilise toxic metals: Part I. Theory and applications☆ , 1997 .

[10]  S. Alonso,et al.  Alkaline activation of metakaolin and calcium hydroxide mixtures: influence of temperature, activator concentration and solids ratio , 2001 .

[11]  J. Deventer,et al.  The geopolymerisation of alumino-silicate minerals , 2000 .

[12]  E. Merz,et al.  Immobilization of intermediate-level wastes in geopolymers , 1994 .

[13]  J.S.J. van Deventer,et al.  The effect of metal contaminants on the formation and properties of waste-based geopolymers , 1999 .

[14]  Hua Xu.  Geopolymerisation of aluminosilicate minerals , 2002 .

[15]  Ángel Palomo,et al.  Alkali-activated cementitious materials: Alternative matrices for the immobilisation of hazardous wastes: Part II. Stabilisation of chromium and lead , 2003 .