A high thermal gradient directional solidification method for growing superalloy single crystals

Abstract The experiments here were conducted at withdrawal rates of 3 mm/min and 1 mm/min using a CMSX-6 and a CMSX-4 superalloy, respectively. The process was assessed in terms of the thermal gradient (GL), structural refinement, microsegregation and porosity distribution, and compared to those using a Bridgman process. The GL of the process was 200–236 K/cm, which was 10–12 times higher than that in the Bridgman process. A more refined microstructure was produced having average primary and secondary dendrite arm spacing values as low as 243 μm and 72 μm, as well as 272 μm and 76 μm in the CMSX-6 and the CMSX-4 castings, respectively. The diameter of γ′ phase in the dendrite core of CMSX-6 and CMSX-4 castings was reduced from 0.8 μm to 0.3 μm and from 1.2 μm to 0.6 μm, respectively. The average areas of (γ′ + γ) eutectic pools became smaller and more homogeneously distributed. The mean pore sizes in the castings were reduced by 57% and 43% for the CMSX-6 and CMSX-4 superalloys, respectively, and the area fractions of the pores in the CMSX-6 and CMSX-4 samples were 16% and 12% of those produced in the Bridgman samples. The segregation coefficients of the major alloying elements were closer to unity than those in the Bridgman process, which indicates that the composition distribution is more uniform.

[1]  B. Shollock,et al.  Directional and single-crystal solidification of Ni-base superalloys: Part I. The role of curved isotherms on grain selection , 2000 .

[2]  D Ma,et al.  Experimental Trials of the Thin Shell Casting (TSC) Technology for Directional Solidification , 2012 .

[3]  D. H. Kirkwood,et al.  A simple model for dendrite arm coarsening during solidification , 1985 .

[4]  Amauri Garcia,et al.  Influence of melt convection on dendritic spacings of downward unsteady-state directionally solidified Al-Cu alloys , 2004 .

[5]  R. Trivedi.  Interdendritic Spacing: Part II. A Comparison of Theory and Experiment , 1984 .

[6]  D. Ma.  Discussion of “thermal and grain-structure simulation in a land-based turbine blade directionally solidifed with the liquid metal cooling process” , 2000 .

[7]  A. F. Giamei,et al.  Liquid metal cooling: A new solidification technique , 1976 .

[8]  Robert F. Singer,et al.  Solidification Characteristics and Segregation Behavior of Nickel-Base Superalloys in Dependence on Different Rhenium and Ruthenium Contents , 2009 .

[9]  Jun Zhang,et al.  High thermal gradient directional solidification and its application in the processing of nickel-based superalloys , 2010 .

[10]  B. Shollock,et al.  Grain structure development in directional solidification of nickel-base superalloys , 2004 .

[11]  P. Sahm,et al.  New Aspects of Freckle Formation During Single Crystal Solidification of CMSX-4 , 2000 .

[12]  T. Pollock,et al.  Thermal Analysis of the Bridgman and Liquid-Metal-Cooled Directional Solidification Investment Casting Processes , 2007 .

[13]  Wilfried Kurz,et al.  Dendrite growth at the limit of stability: tip radius and spacing , 1981 .

[14]  H. Brody.  Solute redistribution in dendritic solidification. , 1965 .

[15]  R. Trivedi,et al.  Microstructure development in the directionally solidified Al–4.0 wt% Cu alloy system , 2001 .

[16]  A. F. Giamei,et al.  On the nature of freckles in nickel base superalloys , 1970 .

[17]  J. Lee,et al.  A Comparative Study of the γ/γ′ Eutectic Evolution During the Solidification of Ni-Base Superalloys , 2011 .

[18]  A. L. Maples,et al.  A thermodynamic prediction for microporosity formation in aluminum-rich Al-Cu alloys , 1987 .

[19]  T. Pollock,et al.  Development of Dendritic Structure in the Liquid-Metal-Cooled, Directional-Solidification Process , 2011 .

[20]  W. Kurz,et al.  Fundamentals of Solidification , 1990 .

[21]  Mustafa Gündüz,et al.  Directional solidification of aluminium -copper alloys , 2002 .

[22]  Norbert Hofmann,et al.  A Novel Casting Process for Single Crystal Gas Turbine Components , 2000 .

[23]  A. F. Giamei,et al.  The origin of freckles in unidirectionally solidified castings , 1970 .

[24]  A. Bührig-Polaczek,et al.  Effect of solidification parameters on the microstructures of superalloy CMSX-6 formed during the downward directional solidification process , 2014 .

[25]  M. Rappaz,et al.  Thermal and grain-structure simulation in a land-based turbine blade directionally solidified with the liquid metal cooling process , 2000 .

[26]  T. Pollock,et al.  Stabilization of thermosolutal convective instabilities in Ni-based single-crystal superalloys: Carbon additions and freckle formation , 2001 .

[27]  Amauri Garcia,et al.  Heat flow parameters affecting dendrite spacings during unsteady-state solidification of Sn-Pb and Al-Cu alloys , 2003 .