Permeability and dynamic elastic moduli of controlled porosity ultra-precision aerostatic structures

Abstract Porous ceramic aerostatic bearings enable precise and smooth motion and improved stiffness compared with widely used orifice restrictor bearings. However, the processing techniques so far used are too complex or rely in lowering the sintering temperature to increase fluid flow. Preferred combinations of fine-grade alumina powders and starch granules were used to produce quality porous structures using fixed processing parameters. Component shrinkage, permeability, pore size and elastic properties were comprehensively characterised as a function of porosity. The new porous ceramic structures exhibited controllable and reproducible permeability and modulus, within the range required for ultra-precision porous aerostatic applications.

[1]  D. Stephenson,et al.  Controlled Porosity Alumina Structures for Ultra‐Precision Hydrostatic Journal Bearings , 2010 .

[2]  J. Corbett,et al.  Porous aerostatic bearings–an updated review , 1998 .

[3]  J. R. Alcock,et al.  The impact of water impregnation method on the accuracy of open porosity measurements , 2002 .

[4]  Arun S. Wagh,et al.  Open pore description of mechanical properties of ceramics , 1991 .

[5]  W. Pabst,et al.  Elasticity of porous ceramics—A critical study of modulus−porosity relations , 2006 .

[6]  R. Angers,et al.  Improvement of the dynamic water-expulsion method for pore size distribution measurements , 1986 .

[7]  M. Bowden,et al.  Porous Ceramics Formed Using Starch Consolidation , 2001 .

[8]  José M.F. Ferreira,et al.  Processing of porous ceramics by ‘starch consolidation’ , 1998 .

[9]  M. Fuji,et al.  Opportunities of porous ceramics fabricated by gelcasting in mitigating environmental issues , 2009 .

[10]  P. Vasconcelos,et al.  Permeability of diatomite layers processed by different colloidal techniques , 2000 .

[11]  R. German.  Powder metallurgy science , 1984 .

[12]  D. Stephenson,et al.  The porosity dependence of flexural modulus and strength for capsule-free hot isostatically pressed porous alumina , 2000 .

[13]  J. Alcock,et al.  The Dependence of Pore Size Distribution on Porosity in Hot Isostatically Pressed Porous Alumina , 2001 .

[14]  K. Phani,et al.  Elastic modulus-porosity relationship for Si3N4 , 1987 .

[15]  Christopher R. Bowen,et al.  Microstructural design of materials for aerostatic bearings , 2008 .

[16]  M. Kosec,et al.  Fabrication, modelling and use of porous ceramics for ultrasonic transducer applications , 2007 .

[17]  W. Duckworth.  Discussion of Ryshkewitch Paper , 1953 .

[18]  R. M. Spriggs.  Expression for Effect of Porosity on Elastic Modulus of Polycrystalline Refractory Materials, Particularly Aluminum Oxide , 1961 .

[19]  R Morrell,et al.  Handbook of properties of technical and engineering ceramics , 1989 .

[20]  Y. Kwan.  Processing and fluid flow characteristics of hot isostatically pressed porous alumina for aerostatic bearing applications , 1996 .

[21]  R. German.  Porosity and particle size effects on the gas flow characteristics of porous metals , 1981 .

[22]  Jw Lemmens.  Impulse Excitation: A Technique for Dynamic Modulus Measurement , 1990 .

[23]  P. Boch,et al.  Measurements of the elastic moduli of ceramics , 1979 .

[24]  A. Nakajima,et al.  Gas permeability and mechanical properties of porous alumina ceramics with unidirectionally aligned pores , 2007 .

[25]  W. Pabst,et al.  Porosity and pore size control in starch consolidation casting of oxide ceramics- : Achievements and problems , 2007 .

[26]  P. R. K. Murti,et al.  Analysis of Externally Pressurized Gas Porous Bearings , 1974 .

[27]  E. M. Cliffel,et al.  Theory and Applications of Controlled Permeability , 1966 .

[28]  W. Pabst,et al.  Elastic properties of porous oxide ceramics prepared using starch as a pore-forming agent , 2009 .