High potential of thin (<1 µm) a‐Si: H/µc‐Si:H tandem solar cells

Silicon based thin tandem solar cells were fabricated by plasma enhanced chemical vapor deposition (PECVD) in a 30 × 30 cm2 reactor. The layer thicknesses of the amorphous top cells and the microcrystalline bottom cells were significantly reduced compared to standard tandem cells that are optimized for high efficiency (typically with a total absorber layer thickness from 1.5 to 3 µm). The individual absorber layer thicknesses of the top and bottom cells were chosen so that the generated current densities are similar to each other. With such thin cells, having a total absorber layer thickness varying from 0.5 to 1.5 µm, initial efficiencies of 8.6–10.7% were achieved. The effects of thickness variations of both absorber layers on the device properties have been separately investigated. With the help of quantum efficiency (QE) measurements, we could demonstrate that by reducing the bottom cell thickness the top cell current density increased which is addressed to back-reflected light. Due to a very thin a-Si:H top cell, the thin tandem cells show a much lower degradation rate under continuous illumination at open circuit conditions compared to standard tandem and a-Si:H single junction cells. We demonstrate that thin tandem cells of around 550 nm show better stabilized efficiencies than a-Si:H and µc-Si:H single junction cells of comparable thickness. The results show the high potential of thin a-Si/µc-Si tandem cells for cost-effective photovoltaics. Copyright © 2010 John Wiley & Sons, Ltd.

[1]  B. Rech,et al.  Flexible amorphous and microcrystalline silicon tandem solar modules in the temporary superstrate concept , 2007 .

[2]  Michio Kondo,et al.  High-rate deposition of microcrystalline silicon p-i-n solar cells in the high pressure depletion regime , 2008 .

[3]  B. Rech,et al.  A new concept for mass production of large area thin-film silicon solar cells on glass , 2006 .

[4]  Susumu Suzuki,et al.  High rate growth of microcrystalline silicon using a high-pressure depletion method with VHF plasma , 2001 .

[5]  L. Feitknecht,et al.  Microcrystalline silicon deposited at high rate on large areas from pure silane with efficient gas utilization , 2007 .

[6]  M. Vaněček,et al.  Influence of Pressure and Plasma Potential on High Growth Rate Microcrystalline Silicon Grown by Very High Frequency Plasma Enhanced Chemical Vapour Deposition , 2006 .

[7]  Bernd Rech,et al.  Challenges in microcrystalline silicon based solar cell technology , 2006 .

[8]  P. Lechner,et al.  Thin film solar modules based on amorphous and microcrystalline silicon , 2003, 3rd World Conference onPhotovoltaic Energy Conversion, 2003. Proceedings of.

[9]  K. Koga,et al.  Highly Stable a-Si:H Films Deposited by Using Multi-Hollow Plasma Chemical Vapor Deposition , 2005 .

[10]  F. Finger,et al.  A constructive combination of antireflection and intermediate-reflector layers for a-Si∕μc-Si thin film solar cells , 2008 .

[11]  J. Müller,et al.  Microcrystalline silicon for large area thin film solar cells , 2003 .

[12]  Reinhard Carius,et al.  Microcrystalline silicon solar cells deposited at high rates , 2005 .

[13]  B. Rech,et al.  Process control of high rate microcrystalline silicon based solar cell deposition by optical emission spectroscopy , 2008 .

[14]  T. Suezaki,et al.  High Efficiency Thin Film Silicon Hybrid Cell and Module with Newly Developed Innovative Interlayer , 2006, 2006 IEEE 4th World Conference on Photovoltaic Energy Conference.

[15]  V. Terrazzoni-Daudrix,et al.  Optimization of amorphous silicon thin film solar cells for flexible photovoltaics , 2008 .

[16]  J. Andreu,et al.  Polycrystalline silicon films obtained by hot-wire chemical vapour deposition , 1994 .

[17]  D. Staebler,et al.  Reversible conductivity changes in discharge‐produced amorphous Si , 1977 .

[18]  P. Buehlmann,et al.  In situ silicon oxide based intermediate reflector for thin-film silicon micromorph solar cells , 2007 .

[19]  H. Stiebig,et al.  Stability of Microcrystalline Silicon Solar Cells with HWCVD Buffer Layer , 2008 .

[20]  Ba Bas Korevaar,et al.  Hydrogenated amorphous silicon deposited at very high growth rates by an expanding Ar-H2-SiH4 plasma , 2001 .