Solid state interfacial reaction of Sn–37Pb and Sn–3.5Ag solders with Ni–P under bump metallization

Abstract Thermal aging is one of the accelerated tests for IC package reliability during manufacturing processes and under actual usage conditions. During the process of thermal aging, intermetallic compounds (IMC) grow continuously due to element diffusion, resulting in their morphology change and thickness increase. In this work, the solid state reaction between electroless Ni–P and two types of Sn-based solders (Sn–3.5Ag and Sn–37Pb) has been investigated. Three distinctive layers, Ni 3 Sn 4 , NiSnP and Ni 3 P, were found between the Sn-containing solders and Ni–P under bump metallization. The growth rates of Ni 3 Sn 4 IMC at different temperatures were obtained from the aged samples and the activation energy of Ni 3 Sn 4 growth was estimated. The kinetic data obtained show that the Ni 3 Sn 4 in the Sn–3.5Ag/Ni–P joints grows much faster than with the Sn–37Pb solder under the same condition. Kirkendall voids are found inside the Ni 3 P layer after thermal aging. The void formation mechanism is due to net Ni out-flux into the solder area.

[1]  K. Tu,et al.  Six cases of reliability study of Pb-free solder joints in electronic packaging technology , 2002 .

[2]  J. Shang,et al.  A comparative fatigue study of solder/electroless-nickel and solder/copper interfaces , 2000 .

[3]  J. Kivilahti,et al.  Effect of dissolution and intermetallic formation on the reliability of FC joints , 1998 .

[4]  Yi-Cheng Liu,et al.  Reflow and property of Al/Cu/electroless nickel/Sn-Pb solder bumps , 1999, ECTC 1999.

[5]  Chwan-Ying Lee,et al.  The interaction kinetics and compound formation between electroless NiP and solder , 1994 .

[6]  Y. C. Chan,et al.  Correlation between Ni_3Sn_4 intermetallics and Ni_3P due to solder reaction-assisted crystallization of electroless Ni–P metallization in advanced packages , 2000 .

[7]  Hyungsuk K. D. Kim,et al.  Spalling of Cu6Sn5 spheroids in the soldering reaction of eutectic SnPb on Cr/Cu/Au thin films , 1996 .

[8]  B. Trumble Get the lead out! [lead free solder] , 1998 .

[9]  Y. C. Chan,et al.  Reliability studies /spl mu/BGA solder joints-effect of Ni-Sn intermetallic compound , 2001 .

[10]  Vesa Vuorinen,et al.  Interfacial reactions between lead-free SnAgCu solder and Ni(P) surface finish on printed circuit boards , 2002 .

[11]  Hyungsuk K. D. Kim,et al.  Ripening‐assisted asymmetric spalling of Cu‐Sn compound spheroids in solder joints on Si wafers , 1996 .

[12]  Studies of electroless nickel under bump metallurgy—Solder interfacial reactions and their effects on flip chip solder joint reliability , 2002 .

[13]  J. Shang,et al.  Thermal stability of electroless-nickel/solder interface: Part B. Interfacial fatigue resistance , 2000 .

[14]  K. Tu,et al.  Tin–lead (SnPb) solder reaction in flip chip technology , 2001 .

[15]  Zhengkui Xu,et al.  Thermal stability of electroless-nickel/solder interface: Part A. interfacial chemistry and microstructure , 2000 .

[16]  M. Li,et al.  Formation of intermetallic compounds in SnPbAg, SnAg, and SnAgCu solders on Ni/Au metallization , 2001 .

[17]  W. T. Chen,et al.  Microstructure, joint strength and failure mechanism of Sn-Ag, Sn-Ag-Cu versus Sn-Pb-Ag solders in BGA packages , 2001, 2001 Proceedings. 51st Electronic Components and Technology Conference (Cat. No.01CH37220).

[18]  C. Kao,et al.  Interactions between solder and metallization during long-term aging of advanced microelectronic packages , 2001 .

[19]  Young-Doo Jeon,et al.  Studies on Ni-Sn intermetallic compound and P-rich Ni layer at the electroless nickel UBM-solder interface and their effects on flip chip solder joint reliability , 2001, 2001 Proceedings. 51st Electronic Components and Technology Conference (Cat. No.01CH37220).

[20]  Y. Chan,et al.  Study of Ni3P growth due to solder reaction-assisted crystallization of electroless Ni-P metallization , 2000 .

[21]  M. He,et al.  Reaction of Sn-Bearing Solders with Nickel-based Under Bump Metallisations , 2004 .

[22]  D. R. Frear,et al.  Solder reaction-assisted crystallization of electroless Ni-P under bump metallization in low cost flip chip technology , 1999 .

[23]  D. R. Frear,et al.  Morphology of interfacial reaction between lead-free solders and electroless Ni–P under bump metallization , 2000 .