Studying the onset of galvanic steel corrosion in situ using thin films: film preparation, characterization and application to pitting

This work reports about a novel approach for investigating surface processes during the early stages of galvanic corrosion of stainless steel in situ by employing ultra-thin films and synchrotron x-radiation. Characterized by x-ray techniques and voltammetry, such films, sputter deposited from austenitic steel, were found representing useful replicas of the target material. Typical for stainless steel, the surface consists of a passivation layer of Fe- and Cr-oxides, a couple of nm thick, that is depleted of Ni. Films of ≈4 nm thickness were studied in situ in an electrochemical cell under potential control (−0.6 to +0.8 V vs Ag/AgCl) during exposure to 0.1 M KCl. Material transport was recorded with better than 1/10 monolayer sensitivity by x-ray spectroscopy. Leaching of Fe was observed in the cathodic range and the therefor necessary reduction of Fe-oxide appears to be accelerated by atomic hydrogen. Except for minor leaching, reduction of Ni, while expected from Pourbaix diagram, was not observed until at a potential of about +0.8 V Cr-oxide was removed from the steel film. After couple of minutes exposure at +0.8 V, the current in the electrochemical cell revealed a rapid pitting event that was simultaneously monitored by x-ray spectroscopy. Continuous loss of Cr and Ni was observed during the induction time leading to the pitting, suggesting a causal connection with the event. Finally, a spectroscopic image of a pit was recorded ex situ with 50 nm lateral and 1 nm depth resolution by soft x-ray scanning absorption microscopy at the Fe L2,3-edges by using a 80 nm film on a SiN membrane, which is further demonstrating the usefulness of thin films for corrosion studies.

[1]  J. Zegenhagen,et al.  Swelling of Steel Film by Hydrogen Absorption at Cathodic Potential in Electrolyte , 2020, physica status solidi (b).

[2]  P. Marcus,et al.  Origin of nanoscale heterogeneity in the surface oxide film protecting stainless steel against corrosion , 2019, npj Materials Degradation.

[3]  E. Lundgren,et al.  Redefining passivity breakdown of super duplex stainless steel by electrochemical operando synchrotron near surface X-ray analyses , 2019, npj Materials Degradation.

[4]  E. Lundgren,et al.  Influence of Surface Strain on Passive Film Formation of Duplex Stainless Steel and Its Degradation in Corrosive Environment , 2019, Journal of The Electrochemical Society.

[5]  O. Magnussen,et al.  Review—In-Situ Surface X-ray Diffraction Studies of Copper Electrodes: Atomic-Scale Interface Structure and Growth Behavior , 2018, Journal of The Electrochemical Society.

[6]  E. Lundgren,et al.  In-situ synchrotron GIXRD study of passive film evolution on duplex stainless steel in corrosive environment , 2018, Corrosion Science.

[7]  P. Marcus,et al.  Progress in corrosion science at atomic and nanometric scales , 2018, Progress in Materials Science.

[8]  David E. Williams,et al.  Surface Layer Formation in the Earliest Stages of Corrosion of Steel in CO2-Saturated Brine at 80°C: Studied by In Situ Synchrotron X-ray Methods , 2018 .

[9]  S. Goto,et al.  Advances in X-Ray/EUV Optics and Components II , 2017 .

[10]  B. Kaulich,et al.  A Sub-Microanalysis Approach in Chemical Characterisation of Gold Nanorods Formed by a Novel Polymer-Immobilised Gold Seeds Base , 2017, Nanomaterials.

[11]  Jingmao Zhao,et al.  Effect of time on the characteristics of passive film formed on stainless steel , 2017 .

[12]  T. Becker,et al.  Emerging surface characterization techniques for carbon steel corrosion: a critical brief review , 2017, Proceedings of the Royal Society A: Mathematical, Physical and Engineering Sciences.

[13]  J. Scully,et al.  Perspective—Localized Corrosion: Passive Film Breakdown vs Pit Growth Stability , 2017 .

[14]  P. Gümpel,et al.  Influence of the surface condition on corrosion behavior of stainless steel , 2016 .

[15]  Gao Yongjin,et al.  The bi-layer structure and the higher compactness of a passive film on nanocrystalline 304 stainless steel , 2016 .

[16]  H. Bluhm,et al.  Liquid/Solid Interfaces Studied by Ambient Pressure HAXPES , 2016 .

[17]  J. Soltis Passivity breakdown, pit initiation and propagation of pits in metallic materials – Review , 2015 .

[18]  N. Krumpa,et al.  Performance of B18, the Core EXAFS Bending Magnet beamline at Diamond , 2013 .

[19]  O. Magnussen,et al.  High-speed in situ surface X-ray diffraction studies of the electrochemical dissolution of Au(001). , 2011, Journal of the American Chemical Society.

[20]  M. Hamdani,et al.  Electrochemical Behaviour of AISI 316 Austenitic Stainless Steel in Acidic Media Containing Chloride Ions , 2011, International Journal of Electrochemical Science.

[21]  S. Allen,et al.  Formation of Delta Ferrite in 9 Wt Pct Cr Steel Investigated by In-Situ X-Ray Diffraction Using Synchrotron Radiation , 2010 .

[22]  Kawal Sawhney,et al.  A Test Beamline on Diamond Light Source , 2010 .

[23]  P. Volovitch,et al.  Atomic emission spectroelectrochemistry applied to dealloying phenomena II. Selective dissolution of iron and chromium during active–passive cycles of an austenitic stainless steel , 2010 .

[24]  J. Baeyens,et al.  Atomic emission spectroelectrochemistry applied to dealloying phenomena: I. The formation and dissolution of residual copper films on stainless steel , 2009 .

[25]  N. Maouche,et al.  Electrochemical Behavior of Polyterthiophene-Coated Types 304 and 316 Stainless Steels and Its Corrosion Performance , 2008 .

[26]  O. Magnussen,et al.  In situ diffraction studies of electrode surface structure during gold electrodeposition , 2008 .

[27]  K. Bhattacharjee,et al.  Probing atomic migration in nanostructured multilayers: application of X-ray standing wave fields. , 2007, Physical review letters.

[28]  M. Jenko,et al.  Electrochemical and XPS studies of the passive film formed on stainless steels in borate buffer and chloride solutions , 2007 .

[29]  Y. F. Cheng,et al.  Mechanism for hydrogen evolution reaction on pipeline steel in near-neutral pH solution , 2007 .

[30]  J. Zegenhagen,et al.  Portable chamber for the study of UHV prepared electrochemical interfaces by hard x-ray diffraction. , 2007, The Review of scientific instruments.

[31]  M Newville,et al.  ATHENA, ARTEMIS, HEPHAESTUS: data analysis for X-ray absorption spectroscopy using IFEFFIT. , 2005, Journal of synchrotron radiation.

[32]  Seok-Jae Lee,et al.  Quantitative analyses of ferrite lattice parameter and solute Nb content in low carbon microalloyed steels , 2005 .

[33]  J. Zegenhagen,et al.  Electrochemical growth of copper on well-defined n-Si(111):H surfaces , 2005 .

[34]  A S Mikhailov,et al.  Sudden Onset of Pitting Corrosion on Stainless Steel as a Critical Phenomenon , 2004, Science.

[35]  D. Landolt,et al.  Passive films on stainless steels—chemistry, structure and growth , 2003 .

[36]  Hsin-Yu Lin,et al.  The mechanism of reduction of iron oxide by hydrogen , 2003 .

[37]  Richard J. Chater,et al.  Why stainless steel corrodes , 2002, Nature.

[38]  G. Frankel Pitting Corrosion of Metals A Review of the Critical Factors , 1998 .

[39]  J. Zegenhagen,et al.  Electrochemical cell for in situ x-ray diffraction under ultrapure conditions , 1998 .

[40]  S. Venugopal,et al.  Influence of strain rate and state-of-stress on the formation of ferrite in stainless steel type AISI 304 during hot working , 1996 .

[41]  J. Zegenhagen,et al.  Surface structure determination with X-ray standing waves , 1993 .

[42]  W. O'grady,et al.  A transmission geometry electrochemical cell for in situ x-ray diffraction , 1993 .

[43]  M. Metikoš-huković,et al.  Oxygen reduction on stainless steel , 1993 .

[44]  F. Walsh,et al.  In situ synchrotron radiation X-ray techniques for studies of corrosion and protection , 1993 .

[45]  R. Kelly,et al.  Passivity breakdown and pitting corrosion of binary alloys , 1991, Nature.

[46]  K. Sieradzki,et al.  Computer simulation of alloy passivation and activation , 1990 .

[47]  G. Materlik,et al.  Structure determination of adsorbates on single crystal electrodes with X-ray standing waves , 1987 .

[48]  R. Mulford,et al.  Surface segregation in austenitic stainless steel , 1982 .

[49]  I. Olefjord,et al.  The Composition of the Surface during Passivation of Stainless Steels , 1982 .

[50]  G. Schmid,et al.  The effect of the Cl− ion on the passive film on anodically polarized 304 stainless steel☆ , 1980 .

[51]  H. Engell,et al.  Investigations of the hydrogen evolution kinetics and hydrogen absorption by iron electrodes during cathodic polarization , 1979 .

[52]  R. P. Frankenthal,et al.  Analysis of the Air‐Formed Oxide Film on a Series of Iron‐Chromium Alloys by Ion‐Scattering Spectrometry , 1976 .

[53]  James H. Scofield,et al.  Relativistic Hartree-Slater Values for K and L X-Ray Emission Rates , 1974 .

[54]  B. Batterman Effect of Dynamical Diffraction in X-Ray Fluorescence Scattering , 1964 .

[55]  L. G. Parratt Surface Studies of Solids by Total Reflection of X-Rays , 1954 .