The influence of ductile tearing on fracture energy in the ductile-to-brittle transition temperature range

The aim of this study is to examine the relationship between fracture energy and the ductile area measured on the fracture surface. Instrumented Charpy tests and fracture toughness tests are performed in the transition temperature range, as well as at lower temperatures. Quantitative fractographic analyses of Charpy specimens reveal a certain proportion of ductile fracture even if the Charpy test is conducted at low temperatures, below the transition temperature. The ductile fracture area situated next to the notch is correlated to fracture energy for all temperatures. In the transition temperature range, fracture energy and the ductile area have a large scatter. Since the limiting event in the development of the ductile area is the initiation of cleavage, the maximum principal stress has been computed in different specimens using the finite element method. It has been shown that the propagating ductile crack does not increase the stress level, but does increase the probability of cleavage fracture through an expansion of the plastic volume where weak points can be found.

[1]  John F. Knott,et al.  Modelling the impact energy in the ductile/brittle transition region of C-Mn multi-run welds , 2000 .

[2]  J. D. Campbell,et al.  The temperature and strain-rate dependence of the shear strength of mild steel , 1970 .

[3]  A. Rosenfield,et al.  Lower-bound fracture toughness of a reactor-pressure-vessel steel , 1981 .

[4]  A. Rossoll,et al.  Mechanical aspects of the Charpy impact test , 1999 .

[5]  C. Prioul,et al.  Fractographic observations of cleavage fracture initiation in a bainitic A508 steel , 1999 .

[6]  D. Curry.  Cleavage micromechanisms of crack extension in steels , 1980 .

[7]  A. Gurson.  Continuum Theory of Ductile Rupture by Void Nucleation and Growth: Part I—Yield Criteria and Flow Rules for Porous Ductile Media , 1977 .

[8]  C. Mcmahon,et al.  Intergranular embrittlement of iron-carbon alloys by impurities , 1974, Metallurgical and Materials Transactions B.

[9]  Stephane Renevey.  Approches globale et locale de la rupture dans le domaine de transition fragile-ductile d'un acier faiblement allie , 1997 .

[10]  G Bernauer,et al.  Modifications of the Beremin model for cleavage fracture in the transition region of a ferritic steel , 1999 .

[11]  A. Mascanzoni,et al.  Microstructure and cleavage resistance of low-carbon bainitic steels , 1977 .

[12]  A. Pineau,et al.  A local criterion for cleavage fracture of a nuclear pressure vessel steel , 1983 .

[13]  Piotr Perzyna,et al.  The constitutive equations for rate sensitive plastic materials , 1963 .

[14]  Viggo Tvergaard,et al.  An analysis of ductile rupture modes at a crack tip , 1987 .

[15]  John R. Rice,et al.  ON THE RELATIONSHIP BETWEEN CRITICAL TENSILE STRESS AND FRACTURE TOUGHNESS IN MILD STEEL , 1973 .