Energy scaling of 4.3 μm room temperature Fe:ZnSe laser.

We demonstrate a fourfold increase of the output energy of the gain-switched mid-IR Fe:ZnSe laser. Iron doping of the ZnSe polycrystalline samples was realized using a postgrowth thermal-diffusion method from the metal film. Gain-switched Er:Cr:YSGG (2.8 μm) laser pumped Fe:ZnSe lasing was studied in a Fabry-Perot cavity over a 236-300 K temperature range. The maximum output energy reached 4.7 mJ at 4.3 μm and 3.6 mJ at 4.37 μm at 236 K and 300 K and was limited only by available pump energy. The laser threshold was about 8 mJ and was practically unchanged over the studied temperature range. The laser slope efficiencies, measured with respect to the input pump energy, decreased from 19% to 16% with an increase of temperature from 236 to 300 K. The output radiation featured a Gaussian spatial profile with M(2) = 2.6.

[1]  V. A. Akimov,et al.  LASERS AND AMPLIFIERS: Efficient lasing in a Fe2+:ZnSe crystal at room temperature , 2006 .

[2]  Ralph H. Page,et al.  Preparation conditions of chromium doped ZnSe and their infrared luminescence properties , 2001 .

[3]  Vladimir V. Fedorov,et al.  Optically dense Fe:ZnSe crystals for energy scaled gain switched lasing , 2010, LASE.

[4]  Petr Koranda,et al.  Room-temperature lasing, gain-switched bulk, tunable Fe:ZnSe laser , 2010, Photonics Europe.

[5]  Jacek Swiderski,et al.  Electrooptically Q-switched mid-infrared Er:YAG laser for medical applications. , 2004, Optics express.

[6]  S. Mirov,et al.  Broadly tunable compact continuous-wave Cr(2+):ZnS laser. , 2002, Optics letters.

[7]  V. A. Akimov,et al.  Vapour growth of II-VI single crystals doped by transition metals for mid-infrared lasers , 2006 .

[8]  Mikhail P. Frolov,et al.  A continuous-wave Fe{sup 2+}:ZnSe laser , 2008 .

[9]  Igor Moskalev,et al.  Progress in Cr2+ and Fe2+ doped mid‐IR laser materials , 2010 .

[10]  A. Burger,et al.  Vapor Growth and Characterization of Cr-Doped ZnSe Crystals , 1999 .

[11]  S A Payne,et al.  4.0-4.5-mum lasing of Fe:ZnSe below 180 K, a new mid-infrared laser material. , 1999, Optics letters.

[12]  V. A. Akimov,et al.  3.77-5.05-μm tunable solid-state lasers based on Fe/sup 2+/-doped ZnSe crystals operating at low and room temperatures , 2006, IEEE Journal of Quantum Electronics.

[13]  Petr Koranda,et al.  Tunable mid-infrared laser properties of Cr2+:ZnMgSe and Fe2+:ZnSe crystals , 2009 .

[14]  S B Mirov,et al.  3.9-4.8 microm gain-switched lasing of Fe:ZnSe at room temperature. , 2005, Optics express.

[15]  S B Mirov,et al.  Hot-pressed ceramic Cr(2+):ZnSe gain-switched laser. , 2006, Optics express.

[16]  Ralph H. Page,et al.  Transition metal-doped zinc chalcogenides: Spectroscopy and laser demonstration of a new class of gain media , 1996 .

[17]  Umit Demirbas,et al.  Synthesis and characterization of diffusion-doped Cr2+:ZnSe and Fe2+:ZnSe , 2006 .

[18]  Tingye Li,et al.  Diffraction loss and selection of modes in maser resonators with circular mirrors , 1965 .