Mg2FeH6 Synthesis Efficiency Map

The influences of the processing parameters on the Mg2FeH6 synthesis yield were studied. Mixtures of magnesium hydride (MgH2) and iron (Fe) were mechanically milled in a planetary ball mill under argon for 0.5-, 1-, 2- and 3-h periods and subsequently sintered at temperatures from 300–500 ∘ C under hydrogen. The reaction yield, phase content and hydrogen storage properties of the received materials were investigated. The morphologies of the powders after synthesis were studied by SEM. The synthesis effectiveness map was presented. The obtained results prove that synthesis parameters, such as the milling time and synthesis temperature, greatly influence the reaction yield and material properties and show that extended mechanical milling may not be beneficial to the reaction efficiency.

[1]  Young-Su Lee,et al.  Low temperature formation of Mg2FeH6 by hydrogenation of ball-milled nano-crystalline powder mixture of Mg and Fe , 2017 .

[2]  R. Zidan,et al.  Modeling of a thermal energy storage system based on coupled metal hydrides (magnesium iron – sodium alanate) for concentrating solar power plants , 2017 .

[3]  F. Trequattrini,et al.  An extensive study of the Mg Fe H material obtained by reactive ball milling of MgH 2 and Fe in a molar ratio 3:1 , 2017 .

[4]  M. Felderhoff,et al.  Development of a heat storage demonstration unit on the basis of Mg2FeH6 as heat storage material and molten salt as heat transfer media , 2017 .

[5]  V. Roche,et al.  Hydrogen storage properties of 2Mg-Fe mixtures processed by hot extrusion at different temperatures , 2017 .

[6]  E. Akiba,et al.  Synthesis of Mg2FeD6 under low pressure conditions for Mg2FeH6 hydrogen storage studies , 2017 .

[7]  J. Huot,et al.  In-situ neutron diffraction investigation of Mg2FeH6 dehydrogenation , 2017 .

[8]  V. Roche,et al.  Characterization of hydrogen storage properties of Mg-Fe-CNT composites prepared by ball milling, hot-extrusion and severe plastic deformation methods , 2016 .

[9]  M. Polański,et al.  Pressurised-cell test stand with oscillating heating for investigation heat transfer phenomena in metal hydride beds , 2016 .

[10]  W. Ding,et al.  Hydrogen storage in Mg2Fe(Ni)H6 nanowires synthesized from coarse-grained Mg and nano sized γ-Fe(Ni) precursors , 2016 .

[11]  Jie Shao,et al.  Effects of Ti-based additives on Mg2FeH6 dehydrogenation properties , 2016 .

[12]  F. Gennari,et al.  Hydrogen cycling properties of xMg–Fe materials (x: 2, 3 and 15) produced by reactive ball milling , 2016 .

[13]  O. Bouaziz,et al.  Light iron and hard magnesium nanocomposites , 2016 .

[14]  S. Deledda,et al.  Effect of synthesis route on the hydrogen storage properties of 2MgH2–Fe compound doped with LiBH4 , 2015 .

[15]  T. Ruskov,et al.  Neutron Powder Diffraction, x-ray absorption and Mössbauer spectroscopy on Mg2FeH6 , 2015 .

[16]  M. Polański,et al.  Why the ball to powder ratio (BPR) is insufficient for describing the mechanical ball milling process , 2014 .

[17]  S. Goumri‐Said,et al.  Hybrid functional calculations of potential hydrogen storage material: Complex dimagnesium iron hydride , 2014 .

[18]  W. Botta,et al.  Hydrogen storage properties of 2Mg–Fe after the combined processes of hot extrusion and cold rolling , 2014 .

[19]  C. Gundlach,et al.  Sorption behavior of the MgH2-Mg2FeH6 hydride storage system synthesized by mechanical milling followed by sintering , 2013 .

[20]  J. Jumas,et al.  Reactivity of complex hydrides Mg2FeH6, Mg2CoH5 and Mg2NiH4 with lithium ion: Far from equilibrium electrochemically driven conversion reactions , 2013 .

[21]  M. Polański,et al.  The influence of the milling time on the yield of Mg2FeH6 from a two-step synthesis conducted in a custom-made reactor , 2013 .

[22]  Anand P. Tiwari,et al.  Studies on de/rehydrogenation characteristics of nanocrystalline MgH2 co-catalyzed with Ti, Fe and Ni , 2013 .

[23]  W. Botta,et al.  Synthesis and hydrogen sorption properties of Mg2FeH6-MgH2 nanocomposite prepared by reactive milling , 2012 .

[24]  S. Deng,et al.  Hydrogen storage performance of 5LiBH4 + Mg2FeH6 composite system , 2012 .

[25]  Henrietta W. Langmi,et al.  Mg2FeH6–LiBH4 and Mg2FeH6–LiNH2 composite materials for hydrogen storage , 2012 .

[26]  C. Kiminami,et al.  2Mg–Fe alloys processed by hot-extrusion: Influence of processing temperature and the presence of MgO and MgH2 on hydrogenation sorption properties , 2011 .

[27]  M. Polański,et al.  Rapid hydrogenation at 30 °C of magnesium (Mg) and iron (Fe) nanocomposite obtained through a decomposition of Mg2FeH6 precursor , 2011 .

[28]  M. Polański,et al.  Synthesis and decomposition mechanisms of Mg2FeH6 studied by in-situ synchrotron X-ray diffraction and high-pressure DSC , 2010 .

[29]  M. Polański,et al.  Dynamic synthesis of ternary Mg2FeH6 , 2010 .

[30]  F. Gennari,et al.  Hydrogen storage properties of MgxFe (x: 2, 3 and 15) compounds produced by reactive ball milling , 2009 .

[31]  F. Gennari,et al.  Thermodynamic and kinetic studies of Mg–Fe–H after mechanical milling followed by sintering , 2008 .

[32]  F. Gennari,et al.  Thermodynamic–kinetic characterization of the synthesized Mg2FeH6–MgH2 hydrides mixture , 2008 .

[33]  O. Morozova,et al.  Controlled mechano-chemical synthesis of nanostructured ternary complex hydride Mg2FeH6 under low-energy impact mode with and without pre-milling , 2004 .

[34]  F. Gennari,et al.  Effect of the nature of the starting materials on the formation of Mg2FeH6 , 2004 .

[35]  D. Wexler,et al.  Formation and environmental stability of nanocrystalline and amorphous hydrides in the 2Mg–Fe mixture processed by controlled reactive mechanical alloying (CRMA) , 2004 .

[36]  J. Lyubina,et al.  Synthesis and decomposition of Mg2FeH6 prepared by reactive milling , 2004 .

[37]  B. Bogdanovic,et al.  Thermodynamics and dynamics of the Mg–Fe–H system and its potential for thermochemical thermal energy storage , 2002 .

[38]  F. Gennari,et al.  Synthesis of Mg2FeH6 by reactive mechanical alloying: formation and decomposition properties , 2002 .

[39]  J. Bobet,et al.  Investigations on the synthesis, structural and microstructural characterizations of Mg-based K2PtCl6 type (Mg2FeH6) hydrogen storage material prepared by mechanical alloying , 2002 .

[40]  Robert Schulz,et al.  Catalytic effect of transition metals on hydrogen sorption in nanocrystalline ball milled MgH2-Tm (Tm=Ti, V, Mn, Fe and Ni) systems , 1999 .

[41]  A. F. Williams,et al.  Dimagnesium iron(II) hydride, Mg2FeH6, containing octahedral FeH64- anions , 1984 .