Surface Layer Modification by Cryogenic Burnishing of Al 7050-T7451 Alloy and Validation with FEM-based Burnishing Model☆

Abstract As one of the chipless machining processes, burnishing has been performed on manufactured components as the final operation to improve the surface integrity, including reduced surface roughness and increased surface and subsurface hardness. Refined surface layers with ultra-fine grains or nano-grains could be generated during the burnishing process due to imposed severe plastic deformation and the associated dynamic recrystallization (DRX). These harder layers with compressive residual stresses induced by the burnishing process also provide added benefits by enhancing wear/corrosion resistance and increasing the fatigue life of the components. The research findings presented in this paper show the effects of cryogenic burnishing with roller burnishing tool on Al 7050-T7451 alloy, using liquid nitrogen as the coolant. Burnishing forces and temperatures are measured to compare the differences between dry and cryogenic burnishing. Higher tangential forces and lower temperatures are observed from cryogenic burnishing due to the work-hardening and the rapid cooling effects introduced by cryogenic burnishing. Also, refined layers with nano-grains (grain size of approximately 40 nm) are formed in the cryogenicallyburnished surface, in which an average hardness increase of 9.5%, 17.5% and 24.8% within the 200 μm depth are achieved in comparison with the hardness values obtained from dry burnishing, at the corresponding burnishing speeds of 25, 50 and 100 m/min. A finite element model (FEM) is developed to simulate the burnishing forces and temperatures for validation of the experimental results, based on the modified Johnson-Cook flow stress model combined with the constitutive equations concerning DRX. Good agreement is obtained between the predicted and experimental results.

[1]  John T. Cammett,et al.  The Influence of Surface Enhancement by Low Plasticity Burnishing on the Corrosion Fatigue Performance of AA7075-T6 , 2004 .

[3]  Miaoquan Li,et al.  The flow behavior and constitutive equations in isothermal compression of 7050 aluminum alloy , 2012 .

[4]  Fritz Klocke,et al.  Finite Element Analysis of the Roller Burnishing Process for Fatigue Resistance Increase of Engine Components , 2011 .

[5]  David A Puleo,et al.  Effect of cryogenic burnishing on surface integrity modifications of Co-Cr-Mo biomedical alloy. , 2013, Journal of biomedical materials research. Part B, Applied biomaterials.

[6]  Yi Wan,et al.  The influence of tool flank wear on residual stresses induced by milling aluminum alloy , 2009 .

[7]  J. Hodowany,et al.  MODELING THE PHYSICS OF METAL CUTTING IN HIGH-SPEED MACHINING , 1998 .

[8]  K Skalski,et al.  Analysis of contact elastic-plastic strains during the process of burnishing , 1995 .

[9]  S. Yang,et al.  CRYOGENIC BURNISHING OF Co-Cr-Mo BIOMEDICAL ALLOY FOR ENHANCED SURFACE INTEGRITY AND IMPROVED WEAR PERFORMANCE , 2012 .

[10]  O. W. Dillon,et al.  Surface Layer Modifications in Co-Cr-Mo Biomedical Alloy from Cryogenic Burnishing , 2011 .

[11]  Shane Y. Hong,et al.  Cooling strategies for cryogenic machining from a materials viewpoint , 1992, Journal of Materials Engineering and Performance.

[12]  John R. Hull,et al.  An overview of Boeing flywheel energy storage systems with high-temperature superconducting bearings , 2010 .

[13]  D. Agard,et al.  Microtubule nucleation by γ-tubulin complexes , 2011, Nature Reviews Molecular Cell Biology.

[14]  Jun Zhou,et al.  Finite Element Model and Analysis for Micro-Cutting of Aluminum Alloy 7050-T7451 , 2012 .

[15]  Chang-Da Wen,et al.  Emissivity characteristics of roughened aluminum alloy surfaces and assessment of multispectral radiation thermometry (MRT) emissivity models , 2004 .

[16]  Andrew D. Sommers,et al.  A thermal model of friction stir welding applied to Sc-modified Al–Zn–Mg–Cu alloy extrusions , 2009 .

[17]  S. Yang,et al.  Ultrafine-grained surface layer on Mg–Al–Zn alloy produced by cryogenic burnishing for enhanced corrosion resistance , 2011 .

[18]  Wit Grzesik,et al.  Modification of surface finish produced by hard turning using superfinishing and burnishing operations , 2012 .

[19]  Yuri Estrin,et al.  Producing bulk ultrafine-grained materials by severe plastic deformation , 2006 .

[20]  A. K. Suri,et al.  Kinetics of dynamic recrystallization in cobalt: A study using the Avrami relation , 2011 .

[21]  Y. Estrin,et al.  Extreme grain refinement by severe plastic deformation: A wealth of challenging science , 2013 .