Analysis of secondary oxide-scale failure at entry into the roll gap

Both numerical analysis based on finite-element (FE) modeling and experimental evidence concerning the secondary oxide-scale failure at entry into the roll gap are presented and reviewed for a better understanding of events at the roll-workpiece interface, in turn, leading to better definition of the boundary conditions for process models. Attention is paid to the two limit modes leading to oxide-scale failure, which were observed earlier during tensile testing under rolling conditions. These are considered in relation to the temperature, the oxide-scale thickness, and other hot-rolling parameters. The mathematical model used for the analysis is composed of macro and micro parts, which allow for simulation of metal/scale flow, heat transfer, cracking of the oxide scale, as well as sliding along the oxide/metal interface and spallation of the scale from the metal surface. The different modes of oxide-scale failure were predicted, taking into account stress-directed diffusion, fracture and adhesion of the oxide scale, strain, strain rate, and temperature. Stalled hot-rolling tests under controlled conditions have been used to verify the types of oxide-scale failure and have shown good predictive capabilities of the model. The stock temperature and the oxide-scale thickness are important parameters, which, depending on other rolling conditions, may cause either through-thickness cracking of the scale at the entry or lead to entry of a nonfractured scale when the scale/metal interface is not strong enough to transmit the metal deformation.

[1]  M. Schütze Mechanical properties of oxide scales , 1995 .

[2]  J. Robertson,et al.  Limits to adherence of oxide scales , 1990 .

[3]  J. Nicholls,et al.  Application of fracture mechanics to failure of surface oxide scales , 1988 .

[4]  M. Ashby,et al.  A second report on sintering diagrams , 1981 .

[5]  H. Riedel Deformation and cracking of thin second-phase layers on deforming metals at elevated temperature , 1982 .

[6]  M. Ashby,et al.  Fracture surface micro-roughness , 1984 .

[7]  K. Kendall The impossibility of comminuting small particles by compression , 1978, Nature.

[8]  William R. D. Wilson,et al.  Surface asperity deformation during sheet forming , 1992 .

[9]  C. J. Smithells,et al.  Metals reference book , 1949 .

[10]  I. V. Samarasekera,et al.  Mathematical modelling of heat flow and deformation during rough rolling , 1993 .

[11]  John H. Beynon,et al.  The tensile failure of mild steel oxides under hot rolling conditions , 1999 .

[12]  M. Ashby,et al.  On grain boundary sliding and diffusional creep , 1971 .

[13]  R Morrell,et al.  Handbook of properties of technical and engineering ceramics , 1989 .

[14]  John H. Beynon,et al.  Finite element model of steel oxide failure during tensile testing under hot rolling conditions , 1999 .

[15]  E. T. Turkdogan,et al.  Scale growth on steels at 1200°C: rationale of rate and morphology , 1984 .

[16]  M. Pietrzyk,et al.  Thermal-mechanical modelling of the flat rolling process , 1991 .