High thermoelectric performance of poly (2,5 -dimethoxyphenylenevinylene) and its derivatives

Abstract Poly(2,5-dimethoxyphenylenevinylene) (PMeOPV) and a series of copolymers consisting of both 2,5-dimethoxy-substituted phenylenevinylene units and unsubstituted units (P(MeOPV- co -PV)) were evaluated from the viewpoint of their thermoelectric properties. Their conjugated polymer films were prepared by pyrolysis of stretched or unstretched films of sulfonium salt precursor polymers, and subsequently doped with iodine vapor to provide electrical conductivity. The power factors P (= S 2 σ ), indicating thermoelectric performance, were calculated with the measured electrical conductivity σ and Seebeck coefficient S of the doped films. PMeOPV showed a higher power factor of 7.1 μW m −1  K −2 at 313 K than that of a camphorsulfonic acid-doped polyaniline as reference. P(MeOPV- co -PV) precursor polymers with less than 20 mol% of MeOPV unit content in the monomer feed were stretchable, therefore providing stretched P(MeOPV- co -PV) films with low MeOPV unit content. The stretching treatment for P(MeOPV- co -PV) enhanced its electrical conductivity, but kept the Seebeck coefficient at nearly the same level as that of unstretched polymers. Consequently a 4.4-fold stretched copolymer exhibited an electrical conductivity of 183.5 S/cm and a Seebeck coefficient of 43.5 μV/K at 313 K, and thus, its power factor at 313 K was over 30 μW m −1  K −2 . To the best of our knowledge, this is the highest thermoelectric performance ever reported among conducting polymers.

[1]  F. E. Karasz,et al.  Analytical methods for molecular weight determination of poly(p-xylylidene dialkyl sulfonium halide): Degree of polymerization of poly(p-phenylene vinylene) precursors , 1989 .

[2]  R. Venkatasubramanian,et al.  Thin-film thermoelectric devices with high room-temperature figures of merit , 2001, Nature.

[3]  Mildred S. Dresselhaus,et al.  Effect of quantum-well structures on the thermoelectric figure of merit. , 1993, Physical review. B, Condensed matter.

[4]  R. Friend,et al.  Studies on the efficient synthesis of poly(phenylenevinylene) (PPV) and poly (dimethoxy phenylenevinylene) (dimethoxy-PPV) , 1991 .

[5]  R. K. Williams,et al.  Filled Skutterudite Antimonides: A New Class of Thermoelectric Materials , 1996, Science.

[6]  Ichiro Terasaki,et al.  Large thermoelectric power in NaCo 2 O 4 single crystals , 1997 .

[7]  Naoki Toshima,et al.  Thermal transporting properties of electrically conductive polyaniline films as organic thermoelectric materials , 2002 .

[8]  D. Rowe.  CRC Handbook of Thermoelectrics , 1995 .

[9]  Yen Wei,et al.  A Study of Leucoemeraldine and the Effect of Redox Reactions on the Molecular-Weight of Chemically Prepared Polyaniline , 1994 .

[10]  J. Schlenoff,et al.  Correlation of Seebeck coefficient and electric conductivity in polyaniline and polypyrrole , 1998 .

[11]  Eric Hu,et al.  Development of a cooling fabric from conducting polymer coated fibres: proof of concept , 2005 .

[12]  D. Bradley.  Precursor-route poly(p-phenylenevinylene): polymer characterisation and control of electronic properties , 1987 .

[13]  M. Hirooka,et al.  Highly conducting poly(phenylene vinylene) derivatives via soluble precursor process , 1987 .

[14]  A. MacDiarmid,et al.  Optical properties of polyaniline , 1993 .

[15]  R. Friend,et al.  Characterisation of poly (phenylenevinylene) by infrared and optical absorption , 1987 .

[16]  Koichi Eguchi,et al.  High‐temperature thermoelectric properties of (Zn1−xAlx)O , 1996 .

[17]  M. Dresselhaus,et al.  Thermoelectric figure of merit of a one-dimensional conductor. , 1993, Physical review. B, Condensed matter.

[18]  Naoki Toshima,et al.  Conductive polymers as a new type of thermoelectric material , 2002 .

[19]  M. Shikano,et al.  Electrical and thermal properties of single-crystalline (Ca2CoO3)0.7CoO2 with a Ca3Co4O9 structure , 2003 .

[20]  T. Tani,et al.  Fabrication of textured thermoelectric layered cobaltites with various rock salt-type layers by using β-Co(OH) 2 platelets as reactive templates , 2004 .

[21]  G. Vineyard,et al.  Semiconductor Thermoelements and Thermoelectric Cooling , 1957 .

[22]  R. E. Gibson,et al.  Di-(α- and β-Substituted Aminoethyl)-benzenes. I. 2,5-bis-(2-Aminoethyl)-hydroquinones , 1949 .

[23]  H. Yan,et al.  Low Thermal Conductivities of Undoped and Various Protonic Acid-Doped Polyaniline Films , 2000 .

[24]  M. P. Walsh,et al.  Quantum Dot Superlattice Thermoelectric Materials and Devices , 2002, Science.

[25]  H. Yan,et al.  Stretched polyaniline films doped by (±)-10-camphorsulfonic acid : Anisotropy and improvement of thermoelectric properties , 2001 .

[26]  R. Lenz,et al.  HIGHLY CONDUCTING, IODINE-DOPED ARYLENE VINYLENE COPOLYMERS WITH DIALKOXYPHENYLENE UNITS , 1989 .

[27]  T. Tani,et al.  Topotactic synthesis of highly-textured thermoelectric cobaltites , 2003 .

[28]  Masaaki Hirooka,et al.  Alkoxy-substituent effect of poly(p-phenylene vinylene) conductivity , 1985 .

[29]  Masaaki Hirooka,et al.  Highly Conducting Poly(P-Phenylene Vinylene) Prepared From Sulfonium Salt , 1985 .

[30]  H. Yan,et al.  Thermoelectric Properties of Alternatively Layered Films of Polyaniline and (±)-10-Camphorsulfonic Acid-Doped Polyaniline , 1999 .

[31]  Tetsuo Tsutsui,et al.  Polyarylenevinylene films prepared from precursor polymers soluble in organic solvents , 1990 .

[32]  George S. Nolas,et al.  Semiconducting Ge clathrates: Promising candidates for thermoelectric applications , 1998 .

[33]  Toshiki Tsubota,et al.  Transport properties and thermoelectric performance of (Zn1–yMgy)1–xAlxO , 1998 .

[34]  Tsunehiro Takeuchi,et al.  An Oxide Single Crystal with High Thermoelectric Performance in Air , 2000 .

[35]  Y. Harima,et al.  Mobilities of charge carriers hopping between π-conjugated polymer chains , 2001 .