FATIGUE CRACK GROWTH AND CLOSURE AT HIGH STRESS RATIOS

— Fatigue crack growth tests have been carried out on a medium carbon structural steel over a wide range of stress ratios, i.e. from 0 to 0.7. All tests were conducted under constant amplitude loading conditions corresponding to growth rates in the Paris regime. Crack closure behaviour was observed experimentally by a surface strain gauge technique, and numerically by a finite element analysis under plane stress condition. While the crack closure could not be detected by experimental measurements at stress ratios equal to or greater than 0.5, the numerical results showed that closure occurred even at high stress ratios up to 0.7. The differences between experimentally and numerically determined crack opening levels were found for each stress ratio. A cause for these differences is discussed. In addition, two new types of crack tip parameters which have been proposed recently are evaluated by finite element analysis and their relevance to fatigue crack growth are discussed. It is concluded that fatigue crack growth rates are substantially determined by the effective stress intensity factor range which is based on the crack closure concept.

[1]  A. F. Grandt,et al.  Three-dimensional crack closure behavior , 1990 .

[2]  R. C. McClung,et al.  High resolution numerical and experimental studies of fatigue cracks , 1991 .

[3]  R. Pippan.  The sensitivity to measure crack closure with strain gauges near the crack tip , 1988 .

[4]  A comparison of acoustic and strain gauge techniques for crack closure , 1975 .

[5]  David L. Davidson,et al.  The dependence of crack closure on fatigue loading variables , 1988 .

[6]  G. Wang,et al.  A strip model for fatigue crack growth predictions under general load conditions , 1991 .

[7]  R. Hertzberg,et al.  On the cyclic behavior of cast and extruded aluminum alloys. Part A: Fatigue crack propagation , 1983 .

[8]  J. Weertman,et al.  Crack closure and crack propagation rates in 7050 aluminum , 1981 .

[9]  D. Holm,et al.  Load Interaction Effects on Compression Fatigue Crack Growth in Ductile Solids , 1988 .

[10]  G.A.O. Davies,et al.  Numerical simulation of fatigue crack growth under complex loading sequences , 1992 .

[11]  R. C. McClung,et al.  On the finite element analysis of fatigue crack closure—2. Numerical results , 1989 .

[12]  V. Sánchez Gálvez,et al.  Modelling plasticity-induced fatigue crack closure , 1990 .

[13]  Robert McClung,et al.  On the finite element analysis of fatigue crack closure—1. Basic modeling issues , 1989 .

[14]  Wei Sun,et al.  Residual stress fields during fatigue crack growth , 1992 .

[15]  W. Elber.  The Significance of Fatigue Crack Closure , 1971 .

[16]  H. Ernst,et al.  Experimental results on fatigue crack closure for two aluminum alloys , 1979 .

[17]  Kiyotsugu Ohji,et al.  Cyclic analysis of a propagating crack and its correlation with fatigue crack growth , 1975 .

[18]  E. Wolf.  Fatigue crack closure under cyclic tension , 1970 .

[19]  Masanori Kawahara,et al.  Analysis on Fatigue Crack Growth Rates Under a Wide Range of Stress Ratios , 1986 .

[20]  Hiroshi Yajima,et al.  Proposal of New Parameter for Fatigue Crack Propagation Rate based upon the ComplianceChanging Phenomena and the Development of its measuring method , 1991 .

[21]  G. Booth,et al.  Correlation of Fatigue Crack Growth Data Obtained at Different Stress Ratios , 1988 .

[22]  J. Newman.  A Finite-Element Analysis of Fatigue Crack Closure , 1976 .

[23]  J. Newman.  A crack-closure model for predicting fatigue crack growth under aircraft spectrum loading , 1981 .

[24]  John W. Hutchinson,et al.  Analysis of Closure in Fatigue Crack Growth , 1978 .