Flammability and mechanical properties of Al(OH)3 and BaSO4 filled polypropylene

The flammability and mechanical properties of Al(OH)3/BaSO4/polypropylene (PP) composites were investigated. The flow, morphological, and thermal properties were also analyzed by melt flow index (MFI), Scanning electron microscopy (SEM), and Differential scanning calorimeter (DSC) studies, respectively. Total filler amount was fixed at 30 wt % to optimize physical characteristics of the composites. In addition to the flame retardant filler Al(OH)3, BaSO4 was used to balance the reduction in impact strength at high filler loadings. Substantial improvement in mechanical properties was achieved for 20 wt % Al(OH)3 (i.e., 10 wt % BaSO4) composition while maximum flammability resistance was obtained for 30 wt % Al(OH)3 composite. SEM studies showed that the presence of aggregated Al(OH)3 particles led to low interfacial adhesion between them and PP matrix ending up with decreased mechanical strength. © 2010 Wiley Periodicals, Inc. J Appl Polym Sci, 2010

[1]  N. A. Isitman,et al.  Nanoclay synergy in flame retarded/glass fibre reinforced polyamide 6 , 2009 .

[2]  Lei Song,et al.  Effects of Charring Agents on the Thermal and Flammability Properties of Intumescent Flame-Retardant HDPE-based Clay Nanocomposites , 2008 .

[3]  A. Mahdavian,et al.  Flame-Retardancy Improvement of Novel Styrene–Maleic Anhydride Based Copolymers , 2007 .

[4]  S. M. B. Nachtigall,et al.  Effect of a macromolecular coupling agent on the properties of aluminum hydroxide/PP composites , 2006 .

[5]  M. M. C. Forte,et al.  Macromolecular coupling agents for flame retardant materials , 2006 .

[6]  H. Demir,et al.  Influence of surface modification of fillers and polymer on flammability and tensile behaviour of polypropylene-composites , 2006 .

[7]  G. Beyer.  Flame retardancy of nanocomposites based on organoclays and carbon nanotubes with aluminium trihydrate , 2006 .

[8]  Martin Schlummer,et al.  Analysis of flame retardant additives in polymer fractions of waste of electric and electronic equipment (WEEE) by means of HPLC-UV/MS and GPC-HPLC-UV. , 2005, Journal of chromatography. A.

[9]  Robert Sporken,et al.  Polymer-layered silicate–carbon nanotube nanocomposites: unique nanofiller synergistic effect , 2004 .

[10]  W. Fan,et al.  Preparation and characterization of flame retardant ABS/montmorillonite nanocomposite , 2004 .

[11]  Jelle Kaspersma,et al.  Fire retardant mechanism of aliphatic bromine compounds in polystyrene and polypropylene , 2002 .

[12]  Zhengjun Li,et al.  Thermal properties and flame retardance of Al(OH)3/polypropylene composites modified by polypropylene grafting with acrylic acid , 2001 .

[13]  R. Li,et al.  Mechanical properties of flame retardant filled polypropylene composites , 2001 .

[14]  R. Li,et al.  Studies on the impact fracture behaviour of flame retardant polymeric material , 2001 .

[15]  S. Boryniec,et al.  Combustion of polymers. Part. III. Fire retardants for polymeric materials , 1999 .

[16]  S. Lomakin,et al.  Polymer flame retardancy : A new approach , 1998 .

[17]  Wen-Yen Chiang,et al.  The improvements in flame retardance and mechanical properties of polypropylene/FR blends by acrylic acid graft copolymerization , 1996 .

[18]  A. Misra,et al.  Flame-Retardant Additives for Polypropylene , 1984 .