Abstract This paper addresses the results of the microstructure and numerical simulation and corrosion analysis and effects of return (DC) current. The results of this research indicate that rail base corrosion can shorten rail’s life from several decades to one year or less compromising integrity and transit system safety. Rail base corrosion is characteristic of rails located in tunnels or wet undergrounds. Rail base corrosion is the result of a combination of factors including humidity, accumulated salts at tie plates and clips, but most importantly the return current (DC) from the transit car traction motors. These factors promote galvanic reactions that increase corrosion rate of the rail. Perhaps the amount of rail lost due to corrosion is no more than 0.005% (6.5 kg km −1 year −1 ) this apparently does not represent a major concern; however, rail base corrosion initiates and propagates by the local removal of the rail forming intricate shapes that act as stress concentrator reducing fatigue life performance. Under extreme circumstances a few grams of lost rail in the right location, with the right geometry and orientation can be responsible for its removal or failure shortening rail’s life to less than a year and can compromise safety. The use of plastic ties and a return stray current system seem to be the most suitable solution for rail base corrosion.
[1]
Stefano Rossi,et al.
Premature corrosion failure of structural highway components made from weathering steel
,
2002
.
[2]
Shi-Lin Chen,et al.
Analysis of rail potential and stray current for Taipei Metro
,
2006,
IEEE Transactions on Vehicular Technology.
[3]
Michele Carboni,et al.
Mode II fatigue failures at rail butt-welds
,
2005
.
[4]
R. J. Hill,et al.
Railroad track electrical impedance and adjacent track crosstalk modeling using the finite-element method of electromagnetic systems analysis
,
1993
.
[5]
Kevin Koch,et al.
Rail Base Corrosion Detection and Prevention
,
2007
.
[6]
Andrea Mariscotti,et al.
Experimental results on low rail-to-rail conductance values
,
2005,
IEEE Transactions on Vehicular Technology.
[7]
Pierre R. Roberge,et al.
Handbook of Corrosion Engineering
,
1999
.
[8]
William D. Callister,et al.
Materials Science and Engineering: An Introduction
,
1985
.
[9]
Peter Mutton,et al.
Failure modes in aluminothermic rail welds under high axle load conditions
,
2004
.