High‐Rate LiFePO4 Electrode Material Synthesized by a Novel Route from FePO4 · 4H2O

A LiFePO4 material with ordered olivine structure is synthesized from amorphous FePO4 · 4H2O through a solid–liquid phase reaction using (NH4)2SO3 as the reducing agent, followed by thermal conversion of the intermediate NH4FePO4 in the presence of LiCOOCH3 · 2H2O. Simultaneous thermogravimetric–differential thermal analysis indicates that the crystallization temperature of LiFePO4 is about 437 °C. Ellipsoidal particle morphology of the resulting LiFePO4 powder with a particle size mainly in the range 100–300 nm is observed by using scanning electron microscopy and transmission electron microscopy. As an electrode material for rechargeable lithium batteries, the LiFePO4 sample delivers a discharge capacity of 167 mA h g–1 at a constant current of 17 mA g–1 (0.1 C rate; throughout this study n C rate means that rated capacity of LiFePO4 (170 mA h g–1) is charged or discharged completely in 1/n hours), approaching the theoretical value of 170 mA h g–1. Moreover, the electrode shows excellent high‐rate charge and discharge capability and high electrochemical reversibility. No capacity loss can be observed up to 50 cycles under 5 C and 10 C rate conditions. With a conventional charge mode, that is, 5 C rate charging to 4.2 V and then keeping this voltage until the charge current is decreased to 0.1 C rate, a discharge capacity of ca. 134 mA h g–1 and cycling efficiency of 99.2–99.6 % can be obtained at 5 C rate.

[1]  J. Shim,et al.  The development of low cost LiFePO4-based high power lithium-ion batteries , 2003 .

[2]  T. Cho,et al.  Synthesis of olivine-type LiFePO4 by emulsion-drying method , 2004 .

[3]  P. Prosini,et al.  Factor affecting rate performance of undoped LiFePO4 , 2004 .

[4]  Shinichi Komaba,et al.  Emulsion drying synthesis of olivine LiFePO4/C composite and its electrochemical properties as lithium intercalation material , 2004 .

[5]  Stefano Passerini,et al.  A New Synthetic Route for Preparing LiFePO4 with Enhanced Electrochemical Performance , 2002 .

[6]  K. S. Nanjundaswamy,et al.  Phospho‐olivines as Positive‐Electrode Materials for Rechargeable Lithium Batteries , 1997 .

[7]  Jingsi Yang,et al.  Nonaqueous Sol-Gel Synthesis of High-Performance LiFePO4 , 2004 .

[8]  Linda F. Nazar,et al.  Approaching Theoretical Capacity of LiFePO4 at Room Temperature at High Rates , 2001 .

[9]  L. Nazar,et al.  Nano-network electronic conduction in iron and nickel olivine phosphates , 2004, Nature materials.

[10]  Sylvain Franger,et al.  LiFePO4 Synthesis Routes for Enhanced Electrochemical Performance , 2002 .

[11]  P. Prosini,et al.  Improved electrochemical performance of a LiFePO4-based composite cathode , 2001 .

[12]  Junwei Jiang,et al.  ARC studies of the thermal stability of three different cathode materials: LiCoO2; Li[Ni0.1Co0.8Mn0.1]O2; and LiFePO4, in LiPF6 and LiBoB EC/DEC electrolytes , 2004 .

[13]  S. Dou,et al.  New approach for synthesis of carbon-mixed LiFePO4 cathode materials , 2004 .

[14]  M. Whittingham,et al.  Hydrothermal synthesis of lithium iron phosphate cathodes , 2001 .

[15]  Yet-Ming Chiang,et al.  Electronically conductive phospho-olivines as lithium storage electrodes , 2002, Nature materials.

[16]  Christopher S. Johnson,et al.  Synthesis and electrochemical analysis of vapor-deposited carbon-coated LiFePO4 , 2005 .

[17]  J. Moon,et al.  Effect of Granulation and Compaction Methods on the Microstructure and Its Related Properties of SOFC Anode , 2003 .

[18]  G. Kim,et al.  Synthesis of LiFePO4 with fine particle by co-precipitation method , 2004 .

[19]  K. Kanamura,et al.  Formation of impurities on phospho-olivine LiFePO4 during hydrothermal synthesis , 2005 .

[20]  W. Jeong,et al.  Synthesis of olivine LiFePO4 cathode materials by mechanical alloying using iron(III) raw material , 2005 .

[21]  Sai-Cheong Chung,et al.  Optimized LiFePO4 for Lithium Battery Cathodes , 2001 .

[22]  Kyusung Park,et al.  Synthesis of LiFePO4 by co-precipitation and microwave heating , 2003 .