Effect of Coarse-Grained Ring on Mechanical Properties and Cutting Performance of 2011 Aluminum Alloy Extruded Bar

The effects of coarse-grained ring on the mechanical properties and cutting performance of 2011 aluminum alloy extruded bars were studied by metallographic microscope, scanning electron microscope, tensile testing machine and high-speed lathe. The results show that the microstructure of aluminum alloy extruded bar was composed of α-Al phase, Al7Cu2Fe phase, CuAl2 phase and SnBi eutectic phase. There was a coarse-grained ring in the aluminum alloy extruded bar. The coarse-grained ring reduced the mechanical properties and cutting performance of the aluminum alloy extruded bar. The aluminum alloy extruded bar with a diameter of 30 mm had a coarse-grained ring depth of 9 mm and lower mechanical properties, whose the tensile strength was 287.9 MPa, the elongation was 17%, the cutting performance was poor and the chips were long. The aluminum alloy extruded bar with a diameter of 40 mm had a coarse-grained ring depth of 1 mm, higher mechanical properties and better cutting performance, whose the tensile strength was 394.5 MPa, the elongation was 23.5%, the chips were fine and uniform.