An investigation of the accelerated thermal degradation of different epoxy resin composites using X-ray microcomputed tomography and optical coherence tomography

Abstract Epoxy resin composites reinforced with hollow glass microspheres, microlight microspheres, 3D parabeam glass, and E-Glass individually were subjected to accelerated thermal degradation conditions. X-ray microcomputed tomography (XμCT) was used to evaluate density changes, reinforcement filler damage, homogeneity, cracks and microcracks in the bulk of the different epoxy resin composites. XμCT 3D images, 2D reconstructed images and voids calculations revealed microspheres damage, filler distributions and showed cracks in all composites with different shapes and volume in response to the thermal degradation conditions. In addition, expansion of air bubbles/voids was observed and recorded in the microsphere and microlight epoxy composite samples. In a complementary way, optical coherence tomography (OCT) was used as a novel optical characterisation technique to study structural changes of the surface and near-surface regions of the composites, uncovering signs of surface shrinkage caused by the thermal treatment. Thus, combining XμCT and OCT proved useful in examining epoxy resin composites' structure, filler–resin interface and surface characteristics.

[1]  F. Awaja,et al.  X-ray Micro Computed Tomography investigation of accelerated thermal degradation of epoxy resin/glass microsphere syntactic foam , 2009 .

[2]  K. Chawla,et al.  Microstructural failure modes in three-phase glass syntactic foams , 2006 .

[3]  Tadeusz Niezgoda,et al.  Analysis of protective structures made of various composite materials subjected to impact , 2008 .

[4]  Shinn-Gwo Hong.  The thermal-oxidative degradation of an epoxy adhesive on metal substrates: XPS and RAIR analyses , 1995 .

[5]  D. Stifter,et al.  Beyond biomedicine: a review of alternative applications and developments for optical coherence tomography , 2007 .

[6]  A. Fercher,et al.  Performance of fourier domain vs. time domain optical coherence tomography. , 2003, Optics express.

[7]  Yu‐Lin Shen,et al.  Thermal expansion of particle-filled plastic encapsulant: a micromechanical characterization , 1998 .

[8]  M. J. Seamark.  Use of syntactic foams of subsea buoyancy , 1991 .

[9]  Avinash C. Kak,et al.  Principles of computerized tomographic imaging , 2001, Classics in applied mathematics.

[10]  Bankim Chandra Ray,et al.  Temperature effect during humid ageing on interfaces of glass and carbon fibers reinforced epoxy composites. , 2006, Journal of colloid and interface science.

[11]  J. Fujimoto,et al.  Optical Coherence Tomography , 1991 .

[12]  B. Bouma,et al.  Handbook of Optical Coherence Tomography , 2001 .

[13]  S. Peters.  Handbook of Composites , 1998 .

[14]  Jean-Claude Grandidier,et al.  Development of experimental, theoretical and numerical tools for studying thermo-oxidation of CFRP composites , 2009 .

[15]  M. Lafarie-Frenot,et al.  Comparison of damage development in C/epoxy laminates during isothermal ageing or thermal cycling , 2006 .

[16]  R. Delobel,et al.  Thermal oxidative degradation of an epoxy resin , 1993 .

[17]  Christoph K. Hitzenberger,et al.  Investigation of polymer and polymer/fibre composite materials with optical coherence tomography , 2008 .

[18]  Carolyn M. Dry,et al.  Procedures developed for self-repair of polymer matrix composite materials , 1996 .

[19]  N. Gimenez,et al.  Hydrolytic ageing of syntactic foams for thermal insulation in deep water: degradation mechanisms and water uptake model , 2006 .

[20]  Michael Pircher,et al.  En-face scanning optical coherence tomography with ultra-high resolution for material investigation. , 2005, Optics express.

[21]  J Decelle,et al.  Oxidation induced shrinkage for thermally aged epoxy networks , 2003 .

[22]  N. Hancox.  Thermal effects on polymer matrix composites: Part 1. Thermal cycling , 1998 .

[23]  V. Altstädt,et al.  Mechanical performance of carbon fibre-reinforced composites based on stitched preforms , 2007 .

[24]  M. A. Verges,et al.  X-ray computed microtomography of internal damage in fiber reinforced polymer matrix composites , 2005 .

[25]  Francesco Aymerich,et al.  Characterization of fracture modes in stitched and unstitched cross-ply laminates subjected to low-velocity impact and compression after impact loading , 2008 .

[26]  S. M. Bishop,et al.  Characterisation of impact damage in skin-stringer composite structures , 1996 .

[27]  I. Bond,et al.  A hollow fibre reinforced polymer composite encompassing self-healing and enhanced damage visibility , 2005 .