A micromechanical study of residual stress and its effect on transverse failure in polymer–matrix composites

Abstract Cure residual stress and its effect on damage in unidirectional fibre-reinforced polymer–matrix composites under transverse loading were studied using a micromechanical unit cell model and the finite element method. The overall residual stress introduced from curing was determined by considering two contributions: volume shrinkage of matrix resin from the crosslink polymerization during isothermal curing and thermal contraction of both resin and fibre as a result of cooling from the curing temperature to room temperature. To examine the effect of residual stress on failure, a model based on the Maximum Principal Stress criterion and stiffness degradation technique was used for damage analysis of the unit cell subjected to mechanical loading after curing. Predicted damage initiation and evolution are clearly influenced by the inclusion of residual stress. Residual stress is always detrimental for transverse compressive loading and pure shear loading. For transverse tensile loading, residual stress is detrimental for relatively low resin strength and beneficial for relatively high resin strength. Failure envelopes were obtained for both biaxial normal loading and combined shear and normal loading and the results show that residual stress results in a shifting and contraction of the failure envelopes.

[1]  Donald M. Blackketter,et al.  Modeling Damage in a Plain Weave Fabric-Reinforced Composite Material , 1993 .

[2]  R. Sakaguchi,et al.  Prediction of composite elastic modulus and polymerization shrinkage by computational micromechanics. , 2004, Dental materials : official publication of the Academy of Dental Materials.

[3]  Börje Andersson,et al.  Micro- and meso-level residual stresses in glass-fiber/vinyl-ester composites , 2000 .

[4]  P. Olivier,et al.  Optimisation of the co-curing of two different composites with the aim of minimising residual curing stress levels , 1998 .

[5]  Scott R. White,et al.  CURE-DEPENDENT VISCOELASTIC RESIDUAL STRESS ANALYSIS OF FILAMENT-WOUND COMPOSITE CYLINDERS , 1998 .

[6]  L. J. Ernst,et al.  Transverse behavior of a unidirectional composite (glass fibre reinforced unsaturated polyester). Part II. Influence of shrinkage strains , 1998 .

[7]  B. K. Fink,et al.  Thermo‐chemical response of vinyl‐ester resin , 2000 .

[8]  Peter Ifju,et al.  Residual strain measurement in composites using the cure-referencing method , 2000 .

[9]  H. Hahn,et al.  Effect of Curing Stresses on the First Ply-failure in Composite Laminates , 1979 .

[10]  Young W. Kwon,et al.  MATRIX DAMAGE OF FIBROUS COMPOSITES: EFFECTS OF THERMAL RESIDUAL STRESSES AND LAYER SEQUENCES , 1997 .

[11]  M. Kumosa,et al.  Residual stresses in unidirectional graphite fiber/polyimide composites as a function of aging , 2004 .

[12]  L. Berglund,et al.  Prediction of matrix-initiated transverse failure in polymer composites , 1996 .

[13]  M. Kumosa,et al.  In-plane shear testing of medium and high modulus woven graphite fiber reinforced/polyimide composites , 2004 .

[14]  Andrew C. Long,et al.  Finite element modelling of damage progression in non-crimp fabric reinforced composites , 2006 .

[15]  Nimmer Rp.  Fiber-matrix interface effects in the presence of thermally induced residual stresses , 1990 .

[16]  M. Kumosa,et al.  An analysis of residual thermal stresses in a unidirectional graphite/PMR-15 composite based on X-ray diffraction measurements , 2001 .

[17]  John W. Gillespie,et al.  Experimental investigation of the cure-dependent response of vinyl ester resin , 2002 .

[18]  J. D. Russell.  Cure shrinkage of thermoset composites , 1993 .

[19]  R. Thomson,et al.  The effect of thermal mismatch on Z-pinned laminated composite structures , 2004 .

[20]  P. D. Soden,et al.  Biaxial test results for strength and deformation of a range of E-glass and carbon fibre reinforced composite laminates: failure exercise benchmark data , 2002 .

[21]  P. D. Soden,et al.  Lamina properties, lay-up configurations and loading conditions for a range of fibre-reinforced composite laminates , 1998 .

[22]  Harold E. Gascoigne,et al.  Residual surface stresses in laminated cross-ply fiber-epoxy composite materials , 1994 .

[23]  C. Sun,et al.  Prediction of composite properties from a representative volume element , 1996 .

[24]  Jan-Anders E. Månson,et al.  Residual stress build-up in thermoset films cured above their ultimate glass transition temperature , 1995 .

[25]  P. Prendergast,et al.  Residual stress due to curing can initiate damage in porous bone cement: experimental and theoretical evidence. , 2002, Journal of biomechanics.

[26]  F. Ellyin,et al.  Evolution and influence of residual stresses/strains of fiber reinforced laminates , 2004 .

[27]  M. M. Aghdam,et al.  More on the effects of thermal residual and hydrostatic stresses on yielding behavior of unidirectional composites , 2003 .

[28]  M. Saka,et al.  Cure shrinkage analysis of epoxy molding compound , 2001 .

[29]  M. A. Stone,et al.  Residual stresses associated with post-cure shrinkage in GRP tubes , 1997 .

[30]  Fuh-Gwo Yuan,et al.  Elastic moduli of brittle matrix composites with interfacial debonding , 1997 .

[31]  Subra Suresh,et al.  Measurement of residual stress in plasma-sprayed metallic, ceramic and composite coatings , 1998 .

[32]  N. Rendler,et al.  Hole-drilling strain-gage method of measuring residual stresses , 1966 .

[33]  Michael R Wisnom,et al.  In-situ measurement of chemical shrinkage of MY750 epoxy resin by a novel gravimetric method , 2004 .

[34]  Sarp Adali,et al.  Optimal temperature profiles for minimum residual stress in the cure process of polymer composites , 2000 .