Measurements of Young's modulus, Poisson's ratio, and tensile strength of polysilicon

New techniques and procedures are described that enable one to measure the mechanical properties of polysilicon films that are 3.5 /spl mu/m thick. Polysilicon is deposited onto a silicon substrate which is then etched away to leave a tensile specimen in the middle of the die. The grip ends of the structure are glued to the grips of a linear air bearing attached to a piezoelectrically actuated loading system. Strain is measured directly on the specimen with laser interferometry. The specimens are fabricated at the Microelectronics Center of North Carolina with their MUMPs process. The results of 48 tests on five different sets of MUMPs specimens yield the following material properties: Young's modulus=169/spl plusmn/6.15 GPa, Poisson's ratio=0.22/spl plusmn/0.011, and tensile strength=1.20/spl plusmn/0.15 GPa These values have a reasonably low coefficient of variation which demonstrates the consistency of both the processing and the measurement techniques.

[1]  Myron A. Jeppesen.  Young's Modulus , 1955 .

[2]  R. E. Bolz,et al.  CRC Handbook of tables for Applied Engineering Science , 1970 .

[3]  Herbert F. Wang,et al.  Single Crystal Elastic Constants and Calculated Aggregate Properties. A Handbook , 1971 .

[4]  W. Sharpe,et al.  New applications of the interferometric strain/displacement gage , 1982 .

[5]  O. Tabata,et al.  Mechanical property measurements of thin films using load-deflection of composite rectangular membranes , 1989 .

[6]  William N. Sharpe,et al.  An interferometric strain-displacement measurement system , 1989 .

[7]  Mehran Mehregany,et al.  Mechanical integrity of polysilicon films exposed to hydrofluoric acid solutions , 1990, IEEE Proceedings on Micro Electro Mechanical Systems, An Investigation of Micro Structures, Sensors, Actuators, Machines and Robots..

[8]  R. Muller,et al.  Measurement of Young's modulus on microfabricated structures using a surface profiler , 1990, IEEE Proceedings on Micro Electro Mechanical Systems, An Investigation of Micro Structures, Sensors, Actuators, Machines and Robots..

[9]  Jari Koskinen,et al.  Microtensile testing of free-standing polysilicon fibers of various grain sizes , 1993 .

[10]  J. Maibach,et al.  Variations in Young's modulus and intrinsic stress of LPCVD-polysilicon due to high-temperature annealing , 1995 .

[11]  Helmut Dr. Klose,et al.  Micromechanics compatible with an 0.8 μm CMOS process , 1995 .

[12]  H. von Philipsborn,et al.  Fracture Strength Of Doped And Undoped Polysilicon , 1995, Proceedings of the International Solid-State Sensors and Actuators Conference - TRANSDUCERS '95.

[13]  R. Howe,et al.  Young's Modulus Of In Situ Phosphorus-doped Polysilicon , 1995, Proceedings of the International Solid-State Sensors and Actuators Conference - TRANSDUCERS '95.

[14]  Victor M. Bright,et al.  Advanced Modeling of Micromirror Devices , 1995 .

[15]  R. Mullen,et al.  Mechanical properties of thick, surface micromachined polysilicon films , 1996, Proceedings of Ninth International Workshop on Micro Electromechanical Systems.

[16]  David T. Read,et al.  Measurements of fracture strength and Young's modulus of surface-micromachined polysilicon , 1996, Photonics West - Micro and Nano Fabricated Electromechanical and Optical Components.

[17]  Bin Yuan,et al.  New test structures and techniques for measurement of mechanical properties of MEMS materials , 1996, Photonics West - Micro and Nano Fabricated Electromechanical and Optical Components.

[18]  Peter M. Osterberg,et al.  Material property measurements of micromechanical polysilicon beams , 1996, Photonics West - Micro and Nano Fabricated Electromechanical and Optical Components.