Sliding wear behaviour of a liquid nitrocarburised precipitation-hardening (PH) stainless steel

A precipitation-hardening stainless steel, of commercial trade name CORRAX, similar to DIN X3CrNiMoAl 13-8-2 grade steel (W.Nr. 1.4534) has been subjected to liquid nitrocarburising in cyanide salt bath to enhance its wear behavior. The wear resistance was evaluated using a pin-on-disk wear testing method with a tungsten carbide counterface against three different steel conditions: nitrocarburised, age-hardened (aged) and solution treated (delivery state). The variation of friction coefficient and wear volume is presented as a function of applied normal load (5, 6, 8 and 10 N) and sliding distance for a constant running speed (0.6 m/s). The pin end (in contact with the disk) had a radius of curvature up to 0.40 mm. The maximum wear resistance of the nitrocarburised specimens is found up to 16 times higher than that of the age-hardened and 31 times higher than that of the solution treated ones. Microscopical observations revealed that the principal wear mechanisms of the nitrocarburized steel are micropolishing and microcutting.

[1]  Yu Zhiwei,et al.  The wear and corrosion properties of stainless steel nitrided by low-pressure plasma-arc source ion nitriding at low temperatures , 2000 .

[2]  S. Antoniou,et al.  Microstructure and tribological behaviour of liquid nitrocarburised tool steels , 2003 .

[3]  J. Baranowska.  Nitride Layer Formation on Chromium-Nickel Steel , 2003 .

[4]  A. Gajek,et al.  Impedance parameters of nitrided 304L stainless steel in an acidified sulphate solution , 2001 .

[5]  M. Somers,et al.  Model Description of Iron-Carbonitride Compound-Layer Formation during Gaseous and Salt-Bath Nitrocarburizing , 1992 .

[6]  S. Mändl,et al.  In situ stress measurements during low-energy nitriding of stainless steel , 2002 .

[7]  D. Bhat,et al.  Surface modification technologies II , 1989 .

[8]  S. Antoniou,et al.  Wear behavior of anti-galling surface textured gray cast iron using pulsed-CO2 laser treatment , 1997 .

[9]  R. Schacherl,et al.  Modelling the Nitriding Kinetics of Iron-Chromium Alloys , 2003 .

[10]  K. Rie,et al.  Further investigation of the structure and properties of austenitic stainless steel after plasma nitriding , 1999 .

[11]  Zhi-wei Yu,et al.  Low pressure plasma arc source ion nitriding of austenitic stainless steel , 2000 .

[12]  M. Pohl,et al.  Effect of plasma nitriding on wear and pitting corrosion resistance of X2 CrNiMoN 22 5 3 duplex stainless steel , 1998 .

[13]  N. Renevier,et al.  Low temperature nitriding of AISI 316L stainless steel and titanium in a low pressure arc discharge , 1999 .