Micro‐ and Frontal Thermal Field‐Flow Fractionation: On the Shear Degradation of Ultra‐high Molar Mass Polymers

Abstract Thermal field‐flow fractionation (TFFF) of ultra‐high molar mass (UHMM) polymers revealed that shear degradation of the macromolecules can appear during the fractionation. Since this problem was not resolved adequately and the conflicting results were published previously, it was useful to analyse in detail the published results, and to complement them by the measurements carried out by newly developed micro‐TFFF in order to find the origin of the previous contradictions. Frontal TFFF performed in standard size channels confirmed definitely that shear degradation of polymer chains was not detectable under the investigated experimental conditions.

[1]  J. Janča.  MICRO-CHANNEL THERMAL FIELD-FLOW FRACTIONATION: ANALYSIS OF ULTRA-HIGH MOLAR MASS POLYMERS AND COLLOIDAL PARTICLES WITH CONSTANT AND PROGRAMMED FIELD FORCE OPERATION , 2002 .

[2]  J. Janča.  MICRO-CHANNEL THERMAL FIELD-FLOW FRACTIONATION: NEW CHALLENGE IN ANALYSIS OF MACROMOLECULES AND PARTICLES , 2002 .

[3]  E. Chubarova.  Thermal Field-Flow Fractionation of Initially Dilute Polymer Solutions as a Shear Degradation Model. Scaling Model of Macromolecule Degradation at Concentrations Exceeding the Critical Entanglement Value , 2000 .

[4]  J. Giddings,et al.  Field-flow fractionation handbook , 2000 .

[5]  V. Nesterov,et al.  Behavior of Macromolecules in Nonhomogeneous Hydrodynamic Fields: Degradation Mechanism of Macromolecules , 1996 .

[6]  Seungho Lee,et al.  Determination of Molecular Weight and Size of Ultrahigh Molecular Weight Polymers Using Thermal Field-Flow Fractionation and Light Scattering , 1995 .

[7]  J. Janča,et al.  Influence of operational parameters on retention of ultra-high molecular weight polystyrenes in thermal field-flow fractionation , 1992 .

[8]  J. Giddings,et al.  Sample overloading effects in polymer characterization by field‐flow fractionation , 1988 .

[9]  J. Janča.  Field-flow fractionation : analysis of macromolecules and particles , 1988 .

[10]  M. N. Myers,et al.  Extension of thermal field-flow fractionation to ultra-high (20 .times. 106) molecular weight polystyrenes , 1985 .

[11]  K. Klepárník,et al.  Determination of Molecular Weight Distribution of Polymers by Thermal Field-Flow Fractionation , 1981 .