Improvement in wear resistance of plasma sprayed yttria stabilized zirconia coating using nanostructured powder

Abstract Plasma sprayed yttria stabilized zirconia coatings were prepared using nanostructured and conventional powders with optimized process parameters for the highest deposition efficiency, the smallest porosity and the highest microhardness. The tribological properties of these coatings against 100C6 steel were then tested with a ball-on-disc arrangement. Results showed that although the friction coefficients of the coatings sprayed using the nanostructured powder were slightly different from those of the coatings sprayed using the conventional powder, the former coatings were more wear resistant than the latter coatings. The wear mechanisms of all the coatings were explained in terms of adhesion-induced spallation and micro-fracturing of lamellae. The improvement in wear resistance of the coatings sprayed using the nanostructured powder could be mainly ascribed to the decrease of micrometer-sized defects such as pores and interlamellar and intralamellar cracks in the coatings.

[1]  Jin-Shun Huang,et al.  Mechanical and tribological properties of plasma-sprayed Cr3C2-NiCr, WC-Co, and Cr2O3 coatings , 1998 .

[2]  Peter R. Strutt,et al.  Abrasive wear characteristics of plasma sprayed nanostructured alumina/titania coatings , 2000 .

[3]  L. Shaw,et al.  The dependency of microstructure and properties of nanostructured coatings on plasma spray conditions , 2000 .

[4]  A. Levy,et al.  Erosion-corrosion of thermal spray coatings , 1990 .

[5]  S. Wen,et al.  The friction and wear performance of plasma-sprayed ceramic coatings at high temperature , 1989 .

[6]  M. Mendelson.  Theoretical evaluation of wear in plasma-sprayed TiO2 against grey cast iron☆ , 1978 .

[7]  C. Berndt,et al.  Integrity of nanostructured partially stabilized zirconia after plasma spray processing , 2001 .

[8]  C. Coddet,et al.  Tribological properties of plasma sprayed alumina-titania coatings : Role and control of the microstructure , 2000 .

[9]  Q. Xue,et al.  The tribological properties of TZP-graphite self-lubricating ceramics , 1996 .

[10]  B. Kear,et al.  Chemical processing and applications for nanostructured materials , 1995 .

[11]  G. Barbezat,et al.  Abrasion, erosion and scuffing resistance of carbide and oxide ceramic thermal sprayed coatings for different applications , 1993 .

[12]  Patrick M. Kelly,et al.  Transformation Toughening in Zirconia‐Containing Ceramics , 2004 .

[13]  A. Heuer,et al.  Microstructural Evolution in a ZrO2 Wt% Y2O3 Ceramic , 1985 .

[14]  D. Lim,et al.  Tribological behaviour of plasma-sprayed zirconia coatings , 1997 .