Thermal shock reliability of a GaN die-attach module on DBA substrate with Ti/Ag metallization by using micron/submicron Ag sinter paste

This study was carried out to evaluate the reliability of GaN die-attached on a direct bonded aluminum (DBA) substrate with Ag sinter joining in up to 1000 harsh thermal shock cycles over a temperature range from −50 °C to 250 °C. For joining the die-attached structure, metallized Ti/Ag was prepared first on the substrates of DBA and GaN chips. A GaN die and DBA substrate were bonded by a micron/submicron Ag sinter paste in air at 250 °C without pressure. The initial die shear strength of the GaN/DBA joint structure, above 33 MPa, was retained up to 250 cycles and then gradually decreased up to 1000 cycles. Microstructural observation by field-emission scanning electron microscopy and energy-dispersive X-ray spectroscopy showed a crack growing inside the Ag/Al bonding interface during thermal cycles due to the large plastic deformation of the Al layer. In addition, with the aid of simulations based on the finite element method, the damage mechanism is discussed in further detail, including the Al grain boundary effect. This study systematically revealed that the mechanism of thermal shock damage of a GaN/DBA module with an Ag sinter joining structure suggests that it can prevent severe damage during thermal shocks in high-temperature applications.

[1]  Shuji Nishimoto,et al.  Novel silver die-attach technology on silver pre-sintered DBA substrates for high temperature applications , 2018, Microelectron. Reliab..

[2]  K. Suganuma,et al.  Bonding technology based on solid porous Ag for large area chips , 2018 .

[3]  Li Ran,et al.  Failure and Reliability Analysis of a SiC Power Module Based on Stress Comparison to a Si Device , 2017, IEEE Transactions on Device and Materials Reliability.

[4]  K. Suganuma,et al.  Macroscale and microscale fracture toughness of microporous sintered Ag for applications in power electronic devices , 2017 .

[5]  K. Suganuma,et al.  Die Bonding Performance Using Bimodal Cu Particle Paste Under Different Sintering Atmospheres , 2017, Journal of Electronic Materials.

[6]  K. Suganuma,et al.  In situ bridging effect of Ag2O on pressureless and low-temperature sintering of micron-scale silver paste , 2017 .

[7]  K. Suganuma,et al.  Mechanical Deformation of Sintered Porous Ag Die Attach at High Temperature and Its Size Effect for Wide-Bandgap Power Device Design , 2017, Journal of Electronic Materials.

[8]  Katsuaki Suganuma,et al.  Thermal Fatigue Behavior of Silicon-Carbide-Doped Silver Microflake Sinter Joints for Die Attachment in Silicon/Silicon Carbide Power Devices , 2017, Journal of Electronic Materials.

[9]  S. T. Chua,et al.  Microstructural studies and bonding strength of pressureless sintered nano-silver joints on silver, direct bond copper (DBC) and copper substrates aged at 300 °C , 2016 .

[10]  K. Suganuma,et al.  Die-attaching silver paste based on a novel solvent for high-power semiconductor devices , 2016, Journal of Materials Science.

[11]  T. Suga,et al.  Transient liquid-phase sintering using silver and tin powder mixture for die bonding , 2016 .

[12]  Katsuaki Suganuma,et al.  Thermostable Ag die-attach structure for high-temperature power devices , 2016, 2018 Second International Symposium on 3D Power Electronics Integration and Manufacturing (3D-PEIM).

[13]  Katsuaki Suganuma,et al.  Addition of SiC Particles to Ag Die-Attach Paste to Improve High-Temperature Stability; Grain Growth Kinetics of Sintered Porous Ag , 2015, Journal of Electronic Materials.

[14]  Katsuaki Suganuma,et al.  Ultra thermal stability of LED die-attach achieved by pressureless Ag stress-migration bonding at low temperature , 2015 .

[15]  F. Giannazzo,et al.  Recent advances on dielectrics technology for SiC and GaN power devices , 2014 .

[16]  Philippe Godignon,et al.  A Survey of Wide Bandgap Power Semiconductor Devices , 2014, IEEE Transactions on Power Electronics.

[17]  Chunqing Wang,et al.  Rapid pressureless low-temperature sintering of Ag nanoparticles for high-power density electronic packaging , 2013 .

[18]  K. Suganuma,et al.  Thermal fatigue of Ag flake sintering die-attachment for Si/SiC power devices , 2013, Journal of Materials Science: Materials in Electronics.

[19]  M. Placidi,et al.  Modelling the metal–semiconductor band structure in implanted ohmic contacts to GaN and SiC , 2013 .

[20]  A. Wu,et al.  Pressureless bonding process using Ag nanoparticle paste for flexible electronics packaging , 2012 .

[21]  K. S. Kim,et al.  Low-temperature low-pressure die attach with hybrid silver particle paste , 2012, Microelectron. Reliab..

[22]  G. Lu,et al.  Investigation of Post-Etch Copper Residue on Direct Bonded Copper (DBC) Substrates , 2011 .

[23]  Kuan Yew Cheong,et al.  Die Attach Materials for High Temperature Applications: A Review , 2011, IEEE Transactions on Components, Packaging and Manufacturing Technology.

[24]  K. Suganuma,et al.  Ultra Heat-Shock Resistant Die Attachment for Silicon Carbide With Pure Zinc , 2010, IEEE Electron Device Letters.

[25]  K. Cheong,et al.  A Review on Die Attach Materials for SiC-Based High-Temperature Power Devices , 2010 .

[26]  H. Ryssel,et al.  NMOS Logic Circuits Using 4H-SiC MOSFETs for High Temperature Applications , 2010 .

[27]  P. Gupta,et al.  Extended Abstracts , 2009, Springer International Publishing.

[28]  R. Fu,et al.  A new method for preparation of direct bonding copper substrate on Al2O3 , 2007 .

[29]  W. Xu,et al.  Development of a directly bonded aluminum/alumina power electronic substrate , 2003 .

[30]  Y. Yoshino,et al.  Thermally Induced Failure of Copper‐Bonded Alumina Substrates for Electronic Packaging , 1992 .

[31]  K. Suganuma,et al.  Thermal Stability of Silver Paste Sintering on Coated Copper and Aluminum Substrates , 2017, Journal of Electronic Materials.