Preparation and properties of solid waste based lightweight plastering gypsum

The lightweight plastering gypsum with excellent heat preservation performance was prepared from β-hemihydrate gypsum obtained by calcining desulfurization gypsum, the polyurethane foam waste modified with water glass, and a composite auxiliary agent composed of ground steel slag and granulated blast-furnace slag. The density of the product is 762.3 kg/m3, the initial setting time is 150 min, the final setting time is 205 min, the flexural strength is 3.1 MPa, the compressive strength is 6.8 MPa, and the thermal conductivity is 0.098 W/(m⋅K).